公开(公告)号：KR1020010028049A

公开(公告)日：2001-04-06

申请号：KR1019990040095

申请日：1999-09-17

Applicant: 제일모직주식회사

Inventor： 정동춘 ,  고영 ,  김명철 ,  김성렬

IPC: C08J9/16

Abstract: PURPOSE: A method for manufacturing foam polystyrene bead is provided which has no decrease in physical properties with reduced changes as time passes, thus has extended storage life by reducing the volatilization rate of foaming agents such as pentane and butane having low boiling point. CONSTITUTION: A foam polystyrene is produced by adding monomers, which have large electro-negativity and contain a second initiator, continuously to a polystyrene polymerized by mixing water and dispersant to prepare aqueous suspension solution then adding styrene monomer containing a first initiator thereto with an elevation of temperature, in order to form a shell on the surface of the polystyrene bead; performing polymerization in the presence of aqueous medium, and impregnating a foaming agent, wherein the monomer is selected from alkyl methacrylate compound, vinyl cyanide compound and combination thereof, the second initiator includes azo-bis-isobutyl nitrile, benzoyl peroxide, and the like, wherein the amount of the monomer is 5-10 wt% based on the weight of the styrene monomer.

Abstract translation: 目的：提供一种制造泡沫聚苯乙烯珠的方法，随着时间的流逝，物理性能随着变化的减小而不降低，从而通过降低发泡剂如戊烷和低沸点丁烷的挥发速度而延长了储存寿命。 构成：通过将具有大的电负性并含有第二引发剂的单体连续加入到通过混合水和分散剂聚合的聚苯乙烯中制备水性悬浮液而制备泡沫聚苯乙烯，然后加入含有第一引发剂的苯乙烯单体， 的温度，以在聚苯乙烯珠的表面上形成壳; 在含水介质的存在下进行聚合，浸渍发泡剂，其中所述单体选自甲基丙烯酸烷基酯化合物，乙烯基氰化合物及其组合，第二引发剂包括偶氮 - 二异丁基腈，过氧化苯甲酰等， 其中单体的量相对于苯乙烯单体的重量为5-10重量％。

公开(公告)号：KR100536089B1

公开(公告)日：2005-12-12

申请号：KR1019990026911

申请日：1999-07-05

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김명철 ,  김성렬

IPC: C08J9/16

Abstract: 본 발명은 발포성 스티렌계 수지를 제조함에 있어서, 글리세릴트리스테아레이트, 에틸렌비닐아세테이트-알코올 코폴리머 및 헥사브로모사이클로도데칸과 디큐밀퍼옥사이드의 혼합물을 스티렌, 아크릴로니트릴, α-메틸스티렌, 및 이들의 혼합물로 구성되는 군으로부터 선택된 스티렌계 단량체 100중량부에 용해하여 분산시키는 단계;와 중합율이 30∼50%에 이르렀을 때 발포제로서 C
n H
2n+2 로 표현되는 휘발성 유기화합물을 첨가하는 단계;와 발포성 스티렌계 수지 입자를 제조한 후, 징크스테아레이트를 첨가하는 단계를 포함하는 난연화 고발포성 스티렌계 수지의 제조방법에 관한 것으로, 발포제 함량이 4% 이하로 환경친화적이고, 최대 발포성이 약 90배로 고발포성이며, 고온고압 발포시 안티-럼핑(Anti-Lumping)효과가 탁월할 뿐만 아니라 난연성을 가짐 으로써 제품 적용에 있어 거의 제한이 없는 장점을 갖는다.

公开(公告)号：KR100516882B1

公开(公告)日：2005-09-23

申请号：KR1019990040095

申请日：1999-09-17

Applicant: 제일모직주식회사

Inventor： 정동춘 ,  고영 ,  김명철 ,  김성렬

IPC: C08J9/16

Abstract: 본 발명은 발포성 폴리스티렌 비드 코어 표면에 화학구조상 전기음성도가 큰 모노머를 공중합시켜 얇은 쉘을 형성시킴으로써 전기음성도가 작은 저비점 펜탄, 부탄등의 발포제가 비드 밖으로 휘발되는 속도를 감속시킨 것을 특징으로 하는, 발포제의 경시변화가 적으면서도 수축 등의 물성 저하가 없는 발포성 폴리스티렌 비드의 제조방법에 관한 것이다.

公开(公告)号：KR1020010008871A

公开(公告)日：2001-02-05

申请号：KR1019990026911

申请日：1999-07-05

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김명철 ,  김성렬

IPC: C08J9/16

Abstract: PURPOSE: A process of preparing the title resin having a foaming agent content of 3 to 4% such as pentane and butadiene regulated by VOCs (volatile organic materials) and restricted in its using amount, imposing almost no restrictions on product suitability and having excellent heat stability is provided, which produces highly-expandable styrene resin capable of being used for an interior material for building or packing material. CONSTITUTION: The highly-expandable styrene resin is prepared by a process consisting of: dispersing 0.5 to 1.0 parts by weight of glyceryl tristearate, 0.05 to 0.5 parts by weight of an ethylenevinylacetate-alcohol copolymer, 0.1 to 1.0 parts by weight of hexabromocyclododecane, 0.05 to 0.5 parts by of dicumylperoxide in 100 parts by weight of a styrene based monomer selected from the group consisting of styrene, acrylonitrile, α-methylstyrene and mixtures thereof; adding less than 4.0% by weight of a volatile organic compound of formula: CnH2n+2 when the polymerization rate attains 30 to 50% ; and adding 0.01 to 0.1 parts by weight of zinc stearate after manufacturing expandable styrene resin particles.

Abstract translation: 目的：制备发泡剂含量为3〜4％的标题树脂的方法，例如由VOC（挥发性有机材料）调节的戊烷和丁二烯，并限制其使用量，对产品适用性几乎没有限制，并具有优异的热 提供了稳定性，其产生能够用于建筑或包装材料的内部材料的高度可发性的苯乙烯树脂。 构成：高发泡苯乙烯树脂通过以下方法制备，该方法包括：将0.5至1.0重量份的三硬脂酸甘油酯，0.05至0.5重量份的乙烯 - 乙酸乙烯酯 - 醇共聚物，0.1至1.0重量份的六溴环十二烷，0.05 在100重量份选自苯乙烯，丙烯腈，α-甲基苯乙烯及其混合物的苯乙烯系单体中加入0.5份过氧化二异丙苯; 当聚合速率达到30〜50％时，加入少于4.0重量％的式CnH2n + 2的挥发性有机化合物; 并在制造可发性苯乙烯树脂颗粒之后加入0.01至0.1重量份的硬脂酸锌。

公开(公告)号：KR1020000055273A

公开(公告)日：2000-09-05

申请号：KR1019990003800

申请日：1999-02-04

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김명철 ,  김성렬

IPC: C08J9/20

Abstract: PURPOSE: A manufacturing method for a high-foaming styrenic resin particle is provided to promote the foaming while reducing contents of a foaming agent and to have an excellent heat-stability almost not generating a lumping in a high-temperature and high-pressure foaming. CONSTITUTION: A manufacturing method for a high-foaming styrenic resin particle uses small amount of foaming agents having a step of an infiltration at 110 through 120 degrees celsius after hydrocarbon gas of 3 to 4 Wt.% as the foaming agent when a polymerization is processed about 50% by suspension-polymerizing a previously dispersed Glyceryl tristearate, Ethylene vinyl acetate-alcohol copolymer and Zinc-stearate in styrenic monomer. The manufactured foaming styrenic resin particles are volatile organic compounds (VOCs) having low contents of foaming agents of a regulated pentane and an affinity to the environment, and have an excellent foaming rate up to 70 times at the maximum, heat-stability and fast forming cycle-time. Thereby, it is expected a variety of application range hereafter.

Abstract translation: 目的：提供高发泡苯乙烯树脂颗粒的制造方法，以促进发泡，同时减少发泡剂的含量，并且具有优异的热稳定性，几乎不会在高温高压发泡中产生结块。 构成：高发泡苯乙烯树脂颗粒的制造方法使用少量发泡剂，当加工聚合时，发泡剂为3〜4Wt％的烃气体后，在110℃〜120℃下具有浸渗步骤的发泡剂 通过将预先分散的三硬脂酸甘油酯，乙烯 - 乙酸乙烯酯 - 醇共聚物和硬脂酸锌悬浮聚合在苯乙烯类单体中约50％。 所制造的发泡苯乙烯树脂颗粒是挥发性有机化合物（VOC），其具有调节戊烷的发泡剂含量低且对环境的亲和性低，并且具有最高达70倍的最大发泡率，热稳定性和快速成型 周期。 因此，预期以下的各种应用范围。

公开(公告)号：KR100536087B1

公开(公告)日：2005-12-12

申请号：KR1019990003800

申请日：1999-02-04

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김명철 ,  김성렬

IPC: C08J9/20

Abstract: 본 발명은 글리세릴트리스테아레이트, 에틸렌비닐아세테이트-알콜 코폴리머 및 징크스테아레이트를 스티렌 모노머내에 미리 분산시킨 것을 현탁중합하여 중합이 30∼50% 정도 진행되었을 때 여기에 발포제로 탄화수소 가스를 3∼4중량% 첨가한 후 발포시키는 것을 특징으로 하는 소량의 발포제를 이용한 고발포성 스티렌 수지 입자의 제조방법에 관한 것으로, 본 발명에 따라 제조된 발포성 스티렌 수지입자는 VOC
S (휘발성유기화학물질류)로 규정된 펜탄의 발포제 함량이 매우 낮아서 일반적인 발포성 수지입자와는 구별되는 환경친화적 제품이며, 낮은 발포제 함량에도 불구하고 발포시 최대 발포배율이 70배로 탁월하고, 뛰어난 열안정성, 빠른 성형 사이클-타임등 그 물성에 있어서도 우수하여 그 적용범위를 확대할 수 있는 장점을 갖는다.

公开(公告)号：KR100315340B1

公开(公告)日：2002-08-01

申请号：KR1019980029099

申请日：1998-07-20

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김명철 ,  김성렬

IPC: C08F12/08

Abstract: 본 발명은 발포성 스티렌 수지 입자를 제조하기 위한 현탁중합법에 있어서 고체미분말, 전해질, 음이온계 계면흡착성 고분자, 및 수용성 과산화염을 조합한 현탁안정제를 사용하려, 고수득율의 좁은 입자 크기 분포를 갖는 발포성 스티렌 수지입자의 제조방법에 관한 것이다. 이러한 과산화염을 포함한 신규의 현탁중합법은 값싼 분산제를 소량 사용함으로써 상업적 효율이 뛰어나고, 중합과정에서 입자간 합일이 일어나지 않기 때문에 입자내부의 부착수분이 없어서 균일한 발포성 스티렌수지 입자를 고수율로 얻을 수 있다. 본 발명의 방법에 따라 제조된 발포체는 상업성이 뛰어나 발포성 스티렌 수지 제조에 이용가치가 높다.

公开(公告)号：KR1020010057522A

公开(公告)日：2001-07-04

申请号：KR1019990061106

申请日：1999-12-23

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김성렬

IPC: C08J9/04

Abstract: PURPOSE: A method for producing polystyrene foam resin is provided for enhancing surface polishing effect and compression strength enough to apply it to various fields by comprising specific quaternary ammonium salt, benzoguanamine and polyethylene wax. CONSTITUTION: The method for producing polystyrene foam resin useful for improving surface polishing effect and compression strength comprises suspending and polymerizing styrene monomer and adding quaternary ammonium salt, benzoguanamine and polyethylene wax as a controlling agent of foam generation. The styrene monomer is selected from a group consisting of styrene monomer, acrylonitrile containing the styrene monomer as a main component and a combination of styrene monomer and alpha-methylstyrene monomer.

Abstract translation: 目的：提供一种生产聚苯乙烯泡沫树脂的方法，用于提高表面抛光效果和压缩强度，足以通过包含特定的季铵盐，苯并胍胺和聚乙烯蜡将其施加到各种领域。 构成：用于提高表面抛光效果和抗压强度的聚苯乙烯发泡树脂的制造方法包括使苯乙烯单体悬浮聚合，加入季铵盐，苯并胍胺和聚乙烯蜡作为发泡剂的控制剂。 苯乙烯单体选自苯乙烯单体，含有苯乙烯单体作为主要成分的丙烯腈和苯乙烯单体与α-甲基苯乙烯单体的组合。

公开(公告)号：KR100516883B1

公开(公告)日：2005-09-23

申请号：KR1019990061106

申请日：1999-12-23

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김성렬

IPC: C08J9/04

Abstract: 본 발명은 스티렌계 단량체를 현탁 중합하여 발포성 폴리스티렌 수지를 제조함에 있어서, 기포 조절제로서 4급 암모늄염, 벤조구아나민 및 폴리에틸렌 왁스를 혼합 사용하는 것을 특징으로 하는 발포성 폴리스티렌 수지의 제조 방법에 관한 것으로서, 본 발명의 방법에 의하여 제조된 발포성 폴리스티렌 수지는 표면 광택 및 압축 강도가 우수하여 어상자용 포장재등 다양한 용도로 사용될 수 있다.

公开(公告)号：KR1020000008971A

公开(公告)日：2000-02-15

申请号：KR1019980029099

申请日：1998-07-20

Applicant: 제일모직주식회사

Inventor： 송강일 ,  정동춘 ,  김명철 ,  김성렬

IPC: C08F12/08

Abstract: PURPOSE: A foaming styrene resin having the uniform particle size of 0.5 to 1.2 millimeter is prepared by a suspension polymerization using aqueous peroxide. CONSTITUTION: The suspension polymerization method comprises: mixing, based on 100 parts by weight of the styrene monomer to be polymerized, 0.25 to 0.50 part by weight of solid fine powder, 0.10 to 0.50 part by weight of an electrolyte and 0.01 to 0.05 part by weight of an anionic surface-absorption polymer with water in a reactor to prepare a suspension; adding a dispersion of the styrene monomer to the suspension under stirring; and adding 0.0002 to 0.005 part by weight of aqueous peroxide based on 100 parts by weight of the styrene monomer, right before heating the reactor to about 90°C. The solid fine powder comprises calcium phosphate. The electrolyte is selected from the group consisting of nitrate, sulfate, carbonate and benzoate. The anionic surface-absorption polymer includes sodium dodecyl benzenesulfonate. The aqueous peroxide includes magnesium persulfate. The styrene monomer further comprises acrylonitrile or alpha-methylstyrene.

Abstract translation: 目的：通过使用过氧化氢水溶液的悬浮聚合制备均匀粒径为0.5〜1.2毫米的发泡苯乙烯树脂。 构成：悬浮聚合法包括：将100重量份待聚合的苯乙烯单体，0.25〜0.50重量份的固体细粉末，0.10〜0.50重量份的电解质和0.01〜0.05重量份的电解质 阴离子表面吸收聚合物与反应器中的水的重量以制备悬浮液; 在搅拌下将苯乙烯单体的分散体加入到悬浮液中; 并且在将反应器加热至约90℃之前，加入基于100重量份苯乙烯单体的0.0002至0.005重量份过氧化氢水溶液。 固体细粉末包括磷酸钙。 电解质选自硝酸盐，硫酸盐，碳酸盐和苯甲酸盐。 阴离子表面吸收聚合物包括十二烷基苯磺酸钠。 过氧化氢水包括过硫酸镁。 苯乙烯单体还包括丙烯腈或α-甲基苯乙烯。