公开(公告)号：KR101477702B1
公开(公告)日：2014-12-30
申请号：KR1020130074529
申请日：2013-06-27
Applicant: 조선대학교산학협력단 , 박근형
CPC classification number: A61L27/306 , A61C8/0012 , A61C8/0013 , A61C13/08 , A61L27/06
Abstract: The present invention relates to a method for manufacturing a dental metal coping using a Ni-Cr-Ti alloy sintered body, wherein the dental metal coping is cheap, retains affinity with gums, facilitates the recovery of ceramic, and has excellent binding property with ceramic and adhering property to gums. The method comprises the steps of preparing Ni, Cr, and Ti powders; mixing 13 wt% of the Cr powder, 10 wt% or less of the Ti powder, and the remainder Ni powder into an alloy powder using a powder mixer; molding the alloy powder into a powder compact type disc having a diameter of 10 mm and a height of 5 mm under a predetermined pressure; sintering the molded disk in argon (Ar) atmosphere; cooling the sintered disc; and processing the cooled disc into a coping for porcelain build-up using CAD/CAM.
Abstract translation: 本发明涉及一种使用Ni-Cr-Ti合金烧结体制造牙科金属制品的方法，其中牙科金属处理便宜，保持与牙龈的亲和力，促进陶瓷的回收，并且与陶瓷具有优异的结合性 并附着在牙龈上。 该方法包括制备Ni，Cr和Ti粉末的步骤; 使用粉末混合机将13重量％的Cr粉末，10重量％以下的Ti粉末和余下的Ni粉末混合成合金粉末; 将合金粉末在预定压力下成型为直径为10mm，高度为5mm的粉末致密型盘; 在氩（Ar）气氛中烧结模制盘; 冷却烧结盘; 并使用CAD / CAM将冷却的盘加工成瓷砖的应对。
-
公开(公告)号：KR1020160077959A
公开(公告)日：2016-07-04
申请号：KR1020140188527
申请日：2014-12-24
Applicant: 조선대학교산학협력단 , 박근형
IPC: C04B35/645
CPC classification number: C04B35/645 , C04B35/0435 , C04B35/2608 , C04B35/46
Abstract: 본발명은 Ni, Cr 및 Ti 분말을준비하되, 13wt%의 Cr 분말, 10wt%이하의 Ti 분말, 잔부의 Ni 분말을분말혼합기를이용하여합금분말로혼합하는단계; 상기합금분말을유압프레스를이용하여직경과높이의길이비가 10 : 5가되도록소정의압력하에압분체의디스크로성형하는단계; 성형된상기디스크를아르곤(Ar) 가스분위기에서소결하는단계; 소결된상기디스크를냉각시키는단계; 상기냉각된디스크를 CAD/CAM을이용하여메탈코핑으로가공하는단계;로이루어짐을특징으로하는치과보철물제작을위한캐드/캠가공용금속소결체제조방법을제공하기위한것으로, 본발명의효과로는가격이저렴하고, 잇몸과의친화성이양호하며, 도재(ceramic)와의결합성및 잇몸과의부착성이우수하면서도금속으로인한블랙검 현상과 Ni 알러지가발생되지않도록하는 Ni-Cr-Ti 합금소결체를이용한도재수복이용이하고매우유용한발명인것이다.
Abstract translation: 本发明提供了一种用于制造用于计算机辅助设计（CAD）/计算机辅助制造（CAM）加工以生产牙植入物的金属颗粒的方法，其包括以下步骤：制备Ni，Cr和Ti粉末（13重量％的Cr 粉末，10重量％以下的Ti粉末和Ni粉末，以剩余的含量提供），并通过混合机混合Ni，Cr和Ti粉末，制成合金粉末; 使用油压机在预定压力下将合金粉末形成为圆盘形的功率压块，使得动力压坯的直径和高度的长度比为10:5; 在Ar（Ar）气体气氛下烧结形成的盘; 冷却烧结盘; 并使用CAD / CAM通过金属配对机加工冷却盘。 根据本发明，可以使用低价格的Ni-Cr-Ti合金烧结体，容易地进行陶瓷修复，表现出优异的亲和性，与陶瓷的粘合性优异，并且具有良好的胶粘附加性，并防止黑色 口香糖和镍由于金属过敏。
-
3.发明申请
公开(公告)号：WO2018174475A1
公开(公告)日：2018-09-27
申请号：PCT/KR2018/003089
申请日：2018-03-16
Applicant: 조선대학교산학협력단
Abstract: 본 발명은 일반적으로 인체내 골에 삽입되어 사용되고 있는 금속재료인 티타늄계 합금 표면에 플라즈마 전해 산화법(Plasma Electrolytic Oxidation)을 이용하여 다공성의 산화 피막을 형성하는 것으로, 더욱 상세하게는 인체를 이루고 있는 많은 이온중에 세포부착과 골 형성으로부터 중요한 역할을 하는 금속(마그네슘, 아연, 스트론튬, 망가니즈)과 실리콘이 함유된 전해질 용액을 사용하여 치과 임플란트 표면에 금속이온 및 실리콘 이온과 칼슘 및 인이 포함된 다공성 산화 피막의 표면을 플라즈마 전해 산화법으로 형성하여 생체활성을 향상시키는 임플란트 제조방법이며, 그 과정은 치과용 티타늄합금을 순차적으로 연마, 미세연마 및 초음파 세척하는 티타늄합금 준비단계, 상기 준비단계에서 준비된 티타늄합금을 전기분해조 양극에 설치하고, 음극은 백금을 설치한 후 전해질 용액을 투입하는 투입단계, 일정한 전압과 전류밀도를 가하여 플라즈마를 생성시켜 티타늄합금에 산화 피막을 형성하는 플라즈마 형성단계 및 상기 플라즈마 형성단계에서 티타늄합금에 산화피막이 형성된 후 에탄올 및 증류수 세척 후 건조시키는 건조단계를 포함하는 플라즈마 전해 산화 공정에서 금속 및 실리콘이 함유된 전해질 조성물 및 그 조성물을 이용하여 금속이온 및 실리콘 이온을 함유하는 수산화아파타이트가 코팅된 치과용 임플란트 제조방법에 관한 것이다. 상기 플라즈마 전해 산화 공정에서 금속 및 실리콘이 함유된 전해질 조성물 및 그 조성물을 이용하여 금속이온 및 실리콘 이온을 함유하는 수산화아파타이트가 코팅된 치과용 임플란트 제조방법으로 인한 효과는 티타늄계 생체합금에 플라즈마 전해 산화공정을 이용하여 치과용 임플란트 표면 처리함으로써 제조공정 과정이 간편하고, 임플란트 제조 시간 및 치료 기간을 저감시키는 효과가 있고, 플라즈마 전해 산화법으로 금속이온과 실리콘 이온을 복합적인 치환을 통해 생체적합성을 지닌 다공성 산화막을 생성하였으며, 종래 금속 산화막보다 두껍고 치밀한 산화막이 제조되며, 금속이온 및 실리콘 이온의 생체활성물질을 포함하여 생체적합성을 빠르게 증가시킴으로써 치과용 임플란트의 초기 고정력을 높여 치료기간을 줄인다.
-
公开(公告)号：KR1020130024130A
公开(公告)日：2013-03-08
申请号：KR1020110087380
申请日：2011-08-30
Abstract: PURPOSE: A metal pellet for PFM(Porcelain Fused to Metal) is provided to improve combination force with ceramic as combination force between metal and porcelain is increased by adding Co and Cr, thereby having optimal biocompatibility. CONSTITUTION: A metal pellet for PFM is composed of 68 wt.% of Co, 27 wt.% of Cr, and 5 wt.% of 27. The pellet is used instead of gold and has excellent biocompatibility.
Abstract translation: 目的：通过添加Co和Cr，通过添加Co和Cr来提高金属和金属之间的组合力，从而提高与陶瓷的组合力，从而提高PFM（瓷料熔融金属）的金属颗粒，从而具有最佳的生物相容性。 构成：用于PFM的金属颗粒由68重量％的Co，27重量％的Cr和5重量％的27组成。使用沉淀代替金并且具有优异的生物相容性。
-
公开(公告)号：KR1020110108031A
公开(公告)日：2011-10-05
申请号：KR1020100027294
申请日：2010-03-26
Applicant: 박근형
IPC: C22C19/05
CPC classification number: C22C19/058 , A61K6/04
Abstract: 본 발명은 Ti 10wt%와 Ni 77wt%, Cr 13wt%로 조성되어짐을 특징으로 하는 치과 금 합금 대체용 티탄크롬니켈합금을 제공하기 위한 것으로, 본 발명 합금은 Ti 첨가로 인하여 매우 가볍고, 도재(ceramic)와 결합성 우수하며, Cr과 Ni함량을 최소화 함으로써 최적의 생체적합성을 갖도록 하고 또 독성이 없는 효과를 갖는다.
또한 본 발명 합금은 치과보철용 합금으로 보다 저렴한 비용에 공급할 수 있는 것이어서 환자의 부담을 최소화할 수 있으며, 잇몸의 블랙 검 현상을 줄여 심미적 효과는 극대화할 수 있는 매우 유용한 발명인 것이다.-
Patent Agency Ranking
公开(公告)号：KR1020080105304A
公开(公告)日：2008-12-04
申请号：KR1020070052719
申请日：2007-05-30
Applicant: 조선대학교산학협력단
Abstract: A titanium nitride method of coating of the alloy for the dental implant is provided to coat the TiN(titanium nitride) on the alloy and to increase stability of a human body. A titanium nitride method of coating of the alloy for the dental implant performs the following steps: a step for washing Ti, Nb, and the Ta powder and removing oxides it does reduction and processes in the hydrogen gas atmosphere of 500‹C for a half hour; a step measuring the washed powders as described above; a step for obtaining the alloy which fuses by using and homogenizes the vacuum arc furnace it becomes the uniform Ti alloy; a step for heat-treating to 1000‹C in the Ar gas atmosphere the process of homogenising temperature, 24 hours the processing time the Ti alloy is put in the furnace; and a step for coating TiN using the RF- magnetron sputter.
Abstract translation: 提供用于牙科植入物的合金的氮化钛涂覆方法以涂覆合金上的TiN（氮化钛）并增加人体的稳定性。 用于牙科植入物的合金的氮化钛涂覆方法进行以下步骤：用于洗涤Ti，Nb和Ta粉末并除去氧化物的步骤在500℃的氢气气氛中还原并处理半 小时; 测量如上所述洗涤过的粉末的步骤; 通过使用并均化真空电弧炉获得熔化的合金的步骤成为均匀的Ti合金; 在氩气氛中将均质化温度，Ti合金放入炉中的加工时间24小时进行热处理至1000℃的步骤; 以及使用RF磁控溅射涂覆TiN的步骤。
-
公开(公告)号：KR101906258B1
公开(公告)日：2018-10-10
申请号：KR1020170159286
申请日：2017-11-27
Applicant: 조선대학교산학협력단
Inventor： 최한철
CPC classification number: A61C13/0012 , A61C8/0015 , A61C13/0016 , A61C13/02 , A61K6/04 , C25D11/026 , C25D11/26
Abstract: 본발명은치과임플란트의제조방법에관한것으로, 보다구체적으로는티타늄계합금에양극산화처리하여나노튜브어레이층을형성시킨다음, 플라즈마전해산화처리함으로써, 표면거칠기를증대시키고, 기능성원소물질의형성을극대화하며, 아나타제상의형성을증대시킬수 있어, 생체적합성을향상시킬수 있는양극산화법과플라즈마전해산화법을이용한치과임플란트의제조방법에관한것이다.
-
8.发明公开
公开(公告)号：KR1020070029912A
公开(公告)日：2007-03-15
申请号：KR1020050084548
申请日：2005-09-12
Applicant: 조선대학교산학협력단
CPC classification number: A61C8/0013 , A61C13/02 , A61C2008/0046 , A61L27/3608 , A61L27/54
Abstract: A manufacturing method of sputtering target using tooth ash powder and a surface reform method of dental implant using the same are provided to reduce dental treatment time by improving assimilability with bones and biocompatibility. The manufacturing method of sputtering target using tooth ash powder includes the steps of: manufacturing a compaction body with a crushing device from a pulled out tooth; and making a sputtering target by burning the compacted tooth. The surface reform method of dental implant using sputtering target using tooth ash powder includes the steps of making a sputtering target by using a pulled out tooth, and applying tooth ash powder on the surface of a dental implant by using a sputtering deposition method.
Abstract translation: 提供使用牙灰粉末的溅射靶的制造方法和使用其的牙科植入物的表面改性方法，以通过提高与骨的同化性和生物相容性来减少牙科治疗时间。 使用牙灰粉末的溅射靶的制造方法包括以下步骤：用拉拔牙来制造具有破碎装置的压实体; 并通过燃烧压实的齿来制造溅射靶。 使用牙灰粉末的使用溅射靶的牙科植入物的表面改性方法包括以下步骤：通过使用拔出的牙齿制造溅射靶，并且通过使用溅射沉积方法将牙灰粉末涂抹在牙科植入物的表面上。
-
9.发明授权플라즈마 전해 산화 공정에서 아연 및 실리콘이 함유된 전해질 조성물 및 그 조성물을 이용하여 아연 및 실리콘 이온을 함유하는 수산화아파타이트가 코팅된 치과용 임플란트 제조방법 有权在等离子体电解氧化过程中含有锌和硅的电解质组合物以及使用该组合物制造涂覆有含有锌和硅离子的羟基磷灰石的牙科植入物的方法
公开(公告)号：KR101835684B1
公开(公告)日：2018-03-07
申请号：KR1020170035326
申请日：2017-03-21
Applicant: 조선대학교산학협력단
CPC classification number: A61C13/0012 , A61C8/0015 , A61C13/0007 , A61K6/033 , A61K6/04 , A61L27/06 , A61L27/32 , A61L2400/18
Abstract: 본발명은일반적으로인체내골에삽입되어사용되고있는금속재료인티타늄계합금표면에플라즈마전해산화법(Plasma Electrolytic Oxidation)을이용하여다공성의산화피막을형성하는것으로, 더욱상세하게는인체를이루고있는많은이온중에세포부착과골 형성으로부터중요한역할을하는아연과실리콘이 함유된전해질용액을사용하여치과임플란트표면에아연및 실리콘이온과칼슘및 인이포함된다공성산화피막의표면을플라즈마전해산화법으로형성하여생체활성을향상시키는임플란트제조방법이며, 그과정은치과용티타늄합금을순차적으로연마, 미세연마및 초음파세척하는티타늄합금준비단계, 상기준비단계에서준비된티타늄합금을전기분해조양극에설치하고, 음극은백금을설치한후 전해질용액을투입하는투입단계, 일정한전압과전류밀도를가하여플라즈마를생성시켜티타늄합금에산화피막을형성하는플라즈마형성단계및 상기플라즈마형성단계에서티타늄합금에산화피막이형성된후 에탄올및 증류수세척후 건조시키는건조단계를포함하는플라즈마전해산화공정에서아연및 실리콘이함유된전해질조성물및 그조성물을이용하여아연및 실리콘이온을함유하는수산화아파타이트가코팅된치과용임플란트제조방법이다. 상기플라즈마전해산화공정에서아연및 실리콘이함유된전해질조성물및 그조성물을이용하여아연및 실리콘이온을함유하는수산화아파타이트가코팅된치과용임플란트제조방법에의한효과는티타늄계생체합금에플라즈마전해산화공정을이용하여치과용임플란트표면처리함으로써제조공정과정이간편하고, 임플란트제조시간및 치료기간을저감시키는효과가있고, 플라즈마전해산화법으로아연과실리콘이온을복합적인치환을통해생체적합성을지닌다공성산화막을생성하였으며, 종래금속산호막보다두껍고치밀한산화막을제조하며, 아연및 실리콘이온의생체활성물질을포함하여생체적합성을증가시켜치과용임플란트의초기고정력을높인다.
Abstract translation: 本发明一般涉及电解等离子体在使用体内骨插入在表面氧化处理后的钛基合金的金属材料，通过使用（等离子体电解氧化）形成的多孔氧化膜，并且更具体地许多组成人体 并使用含有锌和硅的电解质溶液中的离子，从而起到从细胞附着和骨形成电解等离子体锌和硅离子和钙和涂膜的多孔氧化物，它包括一个牙科植入物的表面的表面中起重要作用通过氧化形成 用于提高生物活性，则处理所述植入物的制造方法是这样的，从顺序制备的钛合金抛光牙科钛合金，精抛光和超声波清洗准备工序至电解阴极的钛合金制备步骤的，一个阳极 是在安装铂之后引入电解质溶液的输入步骤，通过施加恒定电压过电流密度来产生等离子体 所形成的氧化膜，以在所述等离子体形成工序和形成反过来钛合金乙醇的氧化膜的形成等离子体的步骤和蒸馏水钛合金，用包含在所述电解等离子体在锌和硅包括干燥所述氧化步骤中，电解质组合物，然后干燥的干燥工序后 使用该组合物涂布含有锌离子和硅离子的羟基磷灰石。 使用包含在氧化处理后的锌和硅，所述电解质组合物和制备含有锌和硅离子的牙科用氢氧化磷灰石涂层的植入物的方法，组合物的效果的等离子体电解，则处理电化学氧化等离子体上的钛基生物合金 通过处理所述植入物表面的牙科的利用，并且是有效的在制造过程中更容易，并降低所述植入物的制造时间和治疗的持续时间，通过取代的组合递送具有由氧化生物相容性血浆锌和硅离子多孔氧化物膜 被创建之前，通过增加生物相容性制备厚和致密的氧化膜比所述珊瑚金属膜，包括锌和硅离子的生物活性物质改善牙科植入物的初步固定。
-
-
-
-
-
-
-
-
-