公开(公告)号：KR100444247B1
公开(公告)日：2004-08-16
申请号：KR1020010076052
申请日：2001-12-04
Applicant: 철강융합신기술연구조합 , 재단법인 포항산업과학연구원 , 포스코강판 주식회사 , 주식회사 포스코
IPC: C23C2/12
Abstract: PURPOSE: A method for manufacturing hot dip aluminum coated stainless steel sheet is provided in which operation is stably performed in annealing process or cooling process by suppressing a chromium oxide film to the maximum through preheating process adopting indirect heating instead of direct fired furnace. CONSTITUTION: In a method for continuously plating stainless steel sheet in a hot dip aluminum coating pot(3), the method for manufacturing hot dip aluminum coated stainless steel sheet(4) by indirect heating comprises a preheating step of indirectly heating the stainless steel sheet(1) in preheating zone(30) at an oxygen concentration of 100 ppm or less and dew point temperature of -40 deg.C or less under the reduction gas atmospheric conditions; annealing step of annealing the preheated stainless steel sheet in annealing zone(50) at a reduction gas atmosphere; and cooling step of cooling the annealed stainless steel sheet in cooling zone(60) to a temperature of the hot dip aluminum coating pot or more at a reduction gas atmosphere, wherein the preheating step is performed in the temperature range of 400 to 500 deg.C, the annealing step is performed at an oxygen concentration of 50 ppm or less and dew point temperature of -30 deg.C or less, wherein the cooling step is performed at a dew point temperature of -20 deg.C or less, and wherein the stainless steel sheet is cooled to a temperature of 680 deg.C or more in the cooling step.
Abstract translation: 目的：提供一种热浸镀铝不锈钢板的制造方法，其通过采用间接加热的预热工艺代替直接燃烧炉，最大限度地抑制氧化铬膜，从而在退火工艺或冷却工艺中稳定地进行操作。 本发明提供一种在热浸镀铝锅（3）中连续镀敷不锈钢钢板的方法，通过间接加热制造热浸镀铝不锈钢钢板（4）的方法包括间接加热不锈钢钢板 （1）在氧气浓度为100ppm以下，露点温度为-40℃以下的预热区域（30）中，在还原气体环境条件下， 在还原气氛下在退火区（50）中对经预热的不锈钢板进行退火的退火步骤; 以及在还原气氛下将冷却区（60）中退火后的不锈钢板冷却至热浸镀铝罐的温度或更高温度的冷却步骤，其中预热步骤在400至500℃的温度范围内进行。 C，退火工序在氧浓度50ppm以下，露点温度-30℃以下的条件下进行，其中，冷却工序在露点温度-20℃以下进行， 其中在冷却步骤中不锈钢板被冷却至680℃或更高的温度。
-
公开(公告)号：KR100290976B1
公开(公告)日：2001-06-01
申请号：KR1019970066196
申请日：1997-12-05
Applicant: 철강융합신기술연구조합 , 재단법인 포항산업과학연구원
IPC: C25F1/00
Abstract: PURPOSE: A low contamination high speed pickling method is provided which is capable of pickling the hot rolled steel sheet with a pickling solution containing low concentrated hydrochloric acid or low concentrated sodium chloride at a low temperature for a short period of time by passing a hot rolled steel sheet through electrochemical treatment process. CONSTITUTION: In pickling a hot rolled steel sheet onto the oxide scale of which cracking is mechanically applied, the low contamination high speed pickling method comprises the processes of charging the steel sheet into an electrolytic cell which is filled up with an HCl solution having a concentration of 0.5 to 5%; and pickling the steel sheet by applying a cathode to the electrolytic cell and impressing a current density of 0.2 to 1.0 A/cm¬2 to the steel sheet at a solution temperature ranging from the room temperature to 80 deg.C for 40 seconds or less, wherein a current density of 0.6 to 1.0 A/cm¬2 is impressed at a solution temperature of 50 to 80 deg.C in case that the concentration of HCl is 0.5%, a current density of 0.2 to 1.0 A/cm¬2 is impressed at a solution temperature of 50 to 80 deg.C in case that the concentration of HCl is 1%, a current density of 0.2 to 1.0 A/cm¬2 is impressed at a solution temperature of 30 to 80 deg.C in case that the concentration of HCl is 2 to 5%, and a mixed pickling solution in which the above HCl is mixed with NaCl having a concentration of 2 to 10% is used as a pickling solution.
-
公开(公告)号：KR100290977B1
公开(公告)日：2001-06-01
申请号：KR1019970069257
申请日：1997-12-16
Applicant: 철강융합신기술연구조합 , 재단법인 포항산업과학연구원
IPC: C25F1/00
Abstract: PURPOSE: A neutral electrolytic pickling method using brine is provided to prevent acidic wastewater and corrosion of a pickling facility generated in conventional pickling process by electrolytically pickling a hot rolled strip in neutral brine. CONSTITUTION: In a method for pickling a hot rolled strip, the neutral electrolytic pickling method using brine comprises the process of performing electrolytic pickling by dipping the hot rolled strip into the brine having a temperature ranging from 35 to 65 deg.C and a concentration ranging from 3.5 to 10% and impressing electric current to the hot rolled strip within the current density range of 1.2 to 2.0 Å/cm¬2 at a duty cycle of 60% or less.
-
公开(公告)号：KR1019990047688A
公开(公告)日：1999-07-05
申请号：KR1019970066196
申请日：1997-12-05
Applicant: 철강융합신기술연구조합 , 재단법인 포항산업과학연구원
IPC: C25F1/00
Abstract: 본 발명은 저공해 고속 산세 방법에 관한 것으로,
기계적으로 산화스케일에 균열을 가한 열연 강판을 산세하는데 있어서,
상기 강판을 0.5-5%농도의 HCl 용액 또는 2-10% 농도의 NaCl과의 혼합 산세액을 채운 전해조에 장입하는 단계; 및
상기 전해조에서 음극에 걸고 실온∼80℃의 온도에서 최대 40초동안 전류 밀도 0.2-1.0A/㎠를 걸어 산세시키는 단계;를 포함하는 저공해 고속 산세 방법이 제공된다.
상기한 바에 따르면, 저농도의 HCl용액 또는 저농도의 NaCl과의 혼합 산세액내에서 실온-80℃ 범위내의 적절한 작업 온도하에, 0.2-1.0A/㎠의 전류 밀도를 인가하는 경우 품질 특성이 우수하면서도, 산세 시간을 40초 이하의 단시간으로 단축할 수 있다.-
公开(公告)号：KR1020030046550A
公开(公告)日：2003-06-18
申请号：KR1020010076052
申请日：2001-12-04
Applicant: 철강융합신기술연구조합 , 재단법인 포항산업과학연구원 , 포스코강판 주식회사 , 주식회사 포스코
IPC: C23C2/12
Abstract: PURPOSE: A method for manufacturing hot dip aluminum coated stainless steel sheet is provided in which operation is stably performed in annealing process or cooling process by suppressing a chromium oxide film to the maximum through preheating process adopting indirect heating instead of direct fired furnace. CONSTITUTION: In a method for continuously plating stainless steel sheet in a hot dip aluminum coating pot(3), the method for manufacturing hot dip aluminum coated stainless steel sheet(4) by indirect heating comprises a preheating step of indirectly heating the stainless steel sheet(1) in preheating zone(30) at an oxygen concentration of 100 ppm or less and dew point temperature of -40 deg.C or less under the reduction gas atmospheric conditions; annealing step of annealing the preheated stainless steel sheet in annealing zone(50) at a reduction gas atmosphere; and cooling step of cooling the annealed stainless steel sheet in cooling zone(60) to a temperature of the hot dip aluminum coating pot or more at a reduction gas atmosphere, wherein the preheating step is performed in the temperature range of 400 to 500 deg.C, the annealing step is performed at an oxygen concentration of 50 ppm or less and dew point temperature of -30 deg.C or less, wherein the cooling step is performed at a dew point temperature of -20 deg.C or less, and wherein the stainless steel sheet is cooled to a temperature of 680 deg.C or more in the cooling step.
Abstract translation: 目的：提供一种制造热浸镀铝不锈钢板的方法，其中通过采用间接加热代替直接烧制炉将氧化铬膜抑制至最大通过预热方法，在退火处理或冷却过程中稳定地进行操作。 构成：在热浸镀铝锅（3）中连续镀不锈钢板的方法中，通过间接加热制造热浸镀铝不锈钢板（4）的方法包括间接加热不锈钢板的预热步骤 （1）在预热区（30）中，在还原气体大气条件下，氧浓度为100ppm以下，露点温度为-40℃以下。 在退火区（50）中在还原气体气氛下退火预热的不锈钢板的退火步骤; 以及将冷却区域（60）中的退火的不锈钢板在还原气体气氛下冷却至所述热浸镀铝锅的温度以上的冷却工序，其中，所述预热工序在400〜500℃的温度范围内进行。 如图C所示，退火工序在氧浓度为50ppm以下，露点温度为-30℃以下的情况下进行，其中，在露点温度为-20℃以下进行冷却工序， 其中在冷却步骤中将不锈钢板冷却至680℃或更高的温度。
-
Patent Agency Ranking
公开(公告)号：KR1019990050194A
公开(公告)日：1999-07-05
申请号：KR1019970069257
申请日：1997-12-16
Applicant: 철강융합신기술연구조합 , 재단법인 포항산업과학연구원
IPC: C25F1/00
Abstract: 본 발명은 열간압연시 열연판의 표면에 발생된 산화피막을 제거하는 산세방법에 관한 것이며; 그 목적은 중성 염수에서 열연강판을 전해산세하여 기존산세공정에서 발생하는 산성폐수 및 산세설비의 부식을 방지할 수 있는 산세방법을 제공함에 있다.
상기 목적을 달성하기 위한 본 발명은, 열연강판을 염수에 침지하고, 이 열연강판에 전류를 인가하여 전해산세하여 이루어지는 염수를 이용한 중성 전해산세방법에 관한 것을 그 요지로 한다.-
公开(公告)号：KR101229075B1
公开(公告)日：2013-02-04
申请号：KR1020060130986
申请日：2006-12-20
Applicant: 재단법인 포항산업과학연구원 , 한국전력공사
CPC classification number: Y02P70/56
Abstract: 본 발명은 용융탄산염 연료 전지용 스택 및 용융탄산염 연료 전지용 분리판의 제조 방법에 관한 것으로서, 상기 스택은 서로 대향하여 위치하는 양극 및 음극 및 상기 양극 및 음극 사이에 위치하며, 상기 양극 및 음극과 접하는 활성 영역 및 상기 양극 및 음극과 접하지 않는 비활성 영역을 포함하는, 용융탄산염 전해질을 포함하는 전해질 막을 포함하는 막-전극 어셈블리 및 상기 막-전극 어셈블리의 양면에 위치하여, 상기 비활성 영역과 접하여 액상 용융부를 형성하는 분리판을 포함하고, 상기 비활성 영역과 접하여 형성되는 액상 용융부는 상기 분리판과 접하게 형성된 아연 코팅층 및 이 아연 코팅층에 형성된 알루미늄 코팅층을 포함한다.
본 발명은 용융탄산염 연료 전지용 분리판 액상 밀봉부에 하층은 아연 코팅층을, 또한 상층은 알루미늄 코팅층을 형성한 이층 코팅층을 형성하여, 650℃ 이하의 공기분위기에서 열처리를 실시하여도 안정하고 품질특성이 우수한 코팅막을 형성시킬 수 있다. 따라서 본 발명은 기존의 방법에 비하여 공정이 간단하고, 열처리 온도가 낮기 때문에 에너지사용이 절감되는 등의 경제성 효과가 있다. 그리고 분리판의 열적변형을 방지할 수 있는 표면처리 방법이기 때문에 분리판의 품질특성을 증가시키는 효과도 있다.
용융탄산염연료전지,분리판,액상밀봉부,이층코팅-
公开(公告)号：KR100992330B1
公开(公告)日：2010-11-05
申请号：KR1020080133947
申请日：2008-12-24
Applicant: 주식회사 포스코 , 재단법인 포항산업과학연구원
Abstract: 본 발명은, 고체 산화물 연료전지(SOFC)용 전해질막 및 셀의 두께 방향 결함을 단시간에 용이하게 검사할 수 있고 검사 신뢰성을 높일 수 있는 검사 장치 및 검사 방법을 제공한다. 본 발명의 일 측면에 따른 SOFC용 전해질막 및 셀 검사 장치는, 검사 대상체의 일 표면 상에 형광액을 도포하는 형광액 도포 장치; 상기 일 표면에 형광액이 도포된 검사 대상체의 반대 표면으로 상기 도포된 형광액을 흡입하기 위한 형광액 흡입 장치; 및 상기 형광액 흡입 장치를 거친 검사 대상체에 대해, 상기 검사 대상체의 반대 표면으로 자외선을 조사하고 상기 검사 대상체의 반대 표면으로부터 상기 검사 대상체의 결함 내의 형광액에 의한 형광을 수광하고 상기 수광된 형광으로부터 상기 검사 대상체의 결함을 측정하는 결함 검사부를 포함한다.
고체 산화물 연료전지, 전해질막, 셀, 결함-
公开(公告)号：KR1020080059114A
公开(公告)日：2008-06-26
申请号：KR1020080025380
申请日：2008-03-19
Applicant: 재단법인 포항산업과학연구원 , 한국전력공사
CPC classification number: Y02E60/526 , Y02P70/56 , H01M8/0295 , H01M2008/147 , H01M2300/0051
Abstract: A method for manufacturing a matrix of a molten carbonate fuel cell is provided to produce the matrix which forms a higher density structure while retaining porosity capable of containing a sufficient amount of electrolyte. A method for manufacturing a matrix of a molten carbonate fuel cell includes the steps of: mixing gamma-LiAlO2 nano-size particles, gamma-LiAlO2 macroparticles, and Al2O3 fiber with a solvent, and ball-milling the mixture for 48-72 hours to obtain a slurry; making the slurry into green sheets using a tape casting method; and drying the green sheets at 25-85 °C. When the slurry is tape-cast, a blade is moved at a speed of 10-40 cm/minute.
Abstract translation: 提供了一种用于制造熔融碳酸盐燃料电池基体的方法，以产生形成较高密度结构的基体，同时保留能够容纳足够量的电解质的孔隙。 一种制造熔融碳酸盐燃料电池基体的方法包括以下步骤：将γ-LiAlO 2纳米尺寸颗粒，γ-LiAlO 2颗粒和Al 2 O 3纤维与溶剂混合，并将混合物球磨48-72小时 获得浆料; 使用流延法将浆料制成生片; 并在25-85℃下干燥生片。 当浆料被流延时，叶片以10-40厘米/分钟的速度移动。
-
公开(公告)号：KR1020080058529A
公开(公告)日：2008-06-26
申请号：KR1020060132278
申请日：2006-12-22
Applicant: 재단법인 포항산업과학연구원 , 한국전력공사
IPC: H01M8/14
CPC classification number: Y02E60/526 , H01M4/8846 , H01M4/8882 , H01M2008/147 , H01M2300/0051
Abstract: A method for impregnating an electrode of a molten carbonate fuel cell with an electrolyte is provided to prevent a drop in height of a fuel cell stack caused by melting of an electrolyte upon driving of the stack, and to realize uniform impregnation of an electrode with an electrolyte. A method for impregnating an electrode of a molten carbonate fuel cell with an electrolyte comprises a step of impregnating a cathode(1) or anode(2) with a eutectic carbonate electrolyte(E) obtained by mixing lithium carbonate or potassium carbonate of sodium carbonate. The cathode is impregnated with the electrolyte by heat treatment at 520-535 deg.C in a gas atmosphere containing hydrogen and nitrogen in a ratio of 0:100 to 20:80.
Abstract translation: 提供了一种用电解质浸渍熔融碳酸盐燃料电池的电极的方法，以防止在堆叠驱动时由电解质熔化引起的燃料电池堆的高度下降，并且实现电极的均匀浸渍 电解质。 用电解质浸渍熔融碳酸盐燃料电池的电极的方法包括用通过混合碳酸锂或碳酸钾的碳酸钠混合获得的共晶碳酸盐电解质（E）浸渍阴极（1）或阳极（2）的步骤。 阴极通过在含有氢和氮的气体气氛中在520-535℃下以0:100至20:80的比例进行热处理而浸渍电解质。
-
-
-
-
-
-
-
-
-