公开(公告)号：KR1020070069948A
公开(公告)日：2007-07-03
申请号：KR1020050132644
申请日：2005-12-28
Applicant: 한국과학기술연구원
Abstract: An amorphous powder core and a manufacturing method thereof are provided to process the amorphous powder at a low pressure by increasing the coupling between powders by forming a rough surface on the amorphous powder. An amorphous powder is formed by curing the powder at a high speed. Copper is coated on the amorphous powder surface. The amorphous powder with the coated copper is oxidized, so that the copper oxide is formed on the surface thereof. An amorphous powder core is obtained by forming the amorphous powder with the copper oxide. The copper is applied on the amorphous powder with a thickness less than 1 um by using an electroless plating scheme. The oxidation of the electroless plating device is performed at a temperature higher than 400 degrees centigrade for less than 60 minutes.
Abstract translation: 提供无定形粉末芯及其制造方法，通过在无定形粉末上形成粗糙表面，通过增加粉末之间的耦合来在低压下加工无定形粉末。 通过高速固化粉末形成无定形粉末。 铜涂在无定形粉末表面上。 具有涂覆铜的无定形粉末被氧化，使得在其表面上形成氧化铜。 通过用氧化铜形成无定形粉末来获得无定形粉末芯。 通过使用化学镀方案将铜施加在厚度小于1μm的无定形粉末上。 化学镀装置的氧化在高于400摄氏度的温度下进行少于60分钟。
-
公开(公告)号：KR100737826B1
公开(公告)日：2007-07-12
申请号：KR1020050132644
申请日：2005-12-28
Applicant: 한국과학기술연구원
Abstract: 본 발명은 고주파특성 및 성형성이 우수한 비정질분말 코어 및 그 제조방법에 관한 것이다. 본 발명에 따른 제조방법은 Fe-Si-B계 비정질분말을 제조하는 단계, 무전해 도금에 의해 Fe-Si-B계 비정질분말표면에 구리를 균일하게 코팅하는 단계, 구리가 코팅된 Fe-Si-B계 비정질분말을 산화시켜 표면에 구리 산화물을 형성시키는 단계, 구리 산화물이 표면에 형성된 Fe-Si-B계 비정질분말을 성형하여 코어를 제조하는 단계를 포함한다. 본 발명에 따른 구리 산화물이 표면에 형성된 Fe-Si-B계 비정질분말은 분말 표면을 거칠게 함으로써 분말 상호간의 결합을 증가시켜 소성변형을 하지 않아 성형이 불가능한 비정질분말을 성형이 가능하게 하며, 표면에 형성된 구리 산화물에 의해 비정질분말 간의 전기적 절연을 향상시켜 고주파대역에서 투자율의 변화가 작고, 자심손실이 작은 비정질분말 코어를 제조할 수 있다.
비정질 분말, 구리, 무전해 도금, 산화, 고주파특성, 자심손실(Core, Loss)
-