Abstract: The sintering temperature of high frequency inductor can be lowered to 1200deg.C from 1400deg.C by adding sintering aid to the powder which is prepared by partial co-precipitation of SnO2 sludge dissolved in Zr4-Ti4 aqueous solution with NH4OH. The obtained powder is sintered at 700-1200deg.C to give TiO4 powder, which is mixed with Zn(NO3)2 as sintering agent, molded into inductor, and sintered at 1100-1400deg.C to give high frequency inductor which maintains induction properties.

Abstract translation: 通过向溶解在Zr4-Ti4水溶液中的SnO 2污泥与NH 4 OH部分共沉淀制备的粉末添加烧结助剂，可以从1400℃将高频电感器的烧结温度降至1200℃。 将得到的粉末在700〜200℃下烧结，得到与Zn（NO 3）2作为烧结剂混合的TiO 4粉末，成型为电感器，并在1100-1400℃烧结，得到保持感应性能的高频电感器 。

公开(公告)号：KR1019970042420A

公开(公告)日：1997-07-24

申请号：KR1019950051091

申请日：1995-12-16

Applicant: 한국과학기술연구원

Inventor： 임경란 ,  장진욱 ,  하조웅

IPC: C04B35/453

Abstract: 본 발명은 고주파 유전체 제조방법에 관한 것으로, SnO
2 입자 위에 Zr
+ , Ti
4+ 수산화물을 침전시키는 방법으로 ZST 분말을 제조한 것이다.
즉, SnO
2 슬러리에 Zr
+ Ti
4+ 의 수용액을, NH
4 OH를 사용하여 침전시키는 부분공침법으로 제조하는 공정과; 상기 제조된 분말을 700∼1200℃에서 하소하는 공정과; 하소하여 얻어진 (Zr
1 -x Snx)TiO
4 분말에 소결조제로 Zn(NO
3 )을 2∼4 mole% 첨가하는 공정과; 제조된 분말을 성형한 후, 1100-1400℃에서 소결하는 공정의 순서로 수행함을 특징으로 한다.
이와 같이 본 발명은 부분공침법을 이용하여 미세한 복합 분말을 제조함으로서 표면 활성에너지를 높여 상의 발달을 빠르게 해주고, 소결 온도를 낮출 수 있으며, 또한, 소결조제를 하소 후에 넣어주어 소결시에 입경계면에 머물게 함으로써 유전 특성을 유지하며, 소결온도를 낮추는 효과가 있다.