Patent Agency Ranking
公开(公告)号：KR1019930011549B1
公开(公告)日：1993-12-10
申请号：KR1019910013922
申请日：1991-08-13
Applicant: 한국과학기술연구원
IPC: H01Q17/00
Abstract: The radio-absorptive material used as an outer tile of building is manufactured by adding the calcinated CuO and Fe2O3 powders to a ferrite powders calcinated at 900 deg.C for 1 hour, and sintering at 1,200 deg.C for 1 hour in an air or under N2 gas atmosphere. The sintered body shows a fine structure according as the liquid phase of CuO-Fe2O3 with radio-absorptive property is present in grain boundary of ferrite.
Abstract translation: 用作建筑外砖的放射性吸收材料是通过将煅烧后的CuO和Fe2O3粉末加入到在900℃煅烧1小时的铁氧体粉末中，并在空气中在1,200℃下烧结1小时来制造的。 在N2气氛下。 该烧结体根据CuO-Fe 2 O 3的液相具有精细的结构，其放射性吸收性存在于铁素体的晶界。
-
-
-
公开(公告)号：KR1019930011547B1
公开(公告)日：1993-12-10
申请号：KR1019910013920
申请日：1991-08-13
Applicant: 한국과학기술연구원
IPC: H01Q17/00
Abstract: The method for mfg. a radio wave absorber is characterized by mixing 66.1 g Fe2O3, 23.1 g ZnO, 8.8 g NiO, 0.5 g MnO2, 0.5 g Co3O4 and 1.0 g CuO, (b) drying and crushing the mixture, (c) calcinating it at 900 deg.C for 2 hr, (d) crushing and moulding it, (e) heating it to the heating rate of 2-12 deg.C/min upto 1250 deg.C for 2-6 hr, and (f) cooling it to the cooling rate of 2-12 deg.C/min to obtain a ferrite sintered body (Ni-Zn).
Abstract translation: 制造方法 其特征在于混合66.1g Fe 2 O 3，23.1g ZnO，8.8g NiO，0.5g MnO 2，0.5g Co 3 O 4和1.0g CuO，（b）干燥并粉碎该混合物，（c）在900℃煅烧。 （d）将其破碎和成型，（e）将其加热至2-12℃/分钟至1250℃的加热速率2-6小时，和（f）将其冷却至 冷却速度为2-12℃/ min，得到铁素体烧结体（Ni-Zn）。
-
公开(公告)号：KR1019930007004A
公开(公告)日：1993-04-22
申请号：KR1019910016924
申请日：1991-09-27
Applicant: 한국과학기술연구원
IPC: H01Q17/00
Abstract: 본 발명은 종래의 페라이트계 전파흡수체에 비해 200-300℃정도 낮은 온도에서 소결가능한 저온소결용 전파흡수체 조성물에 관한 것이다.
본 발명의 조성의 CuO 5-15몰%, NiO 7-21몰%, ZnO 18-33몰% 이하의 Fe
2 O
3 로 이루어져 있다. 이같은 본 발명은 UHF대역과 VHF대역을 동시에 커버하는 넓은 주파수 대역 특성을 나타냄과 아울러 소결시 소결온도가 900-950℃로 낮음에 따라 제조비용이 낮다는 이점이 있다.
-
-
-
-
-
-