公开(公告)号：JP2007284799A

公开(公告)日：2007-11-01

申请号：JP2007158880

申请日：2007-06-15

Applicant: Ati Properties Inc ,  エイティーアイ・プロパティーズ・インコーポレーテッド

Inventor： SORACE DOMINIC A ,  GRUBB JOHN F

IPC: C21D8/02 ,  C22C38/00 ,  C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L29/08

CPC classification number: C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L67/02 ,  Y10S707/959 ,  Y10S707/99945

Abstract: PROBLEM TO BE SOLVED: To provide an austenitic stainless steel exerting a corrosion resistance in an environment of concentrated sulfuric acid.
SOLUTION: The austenitic stainless steel is an alloy having a composition comprising, by weight, about 0.025% or less carbon, about 0.5 to about 4.1% manganese, about 5.5 to about 6.2% silicon, about 11 to about 15% chromium, about 9.0 to about 15.5% nickel, about 0.8 to about 1.2% molybdenum, about 0.8 to about 2% copper and the balance essentially being iron and unavoidable impurities. The composition results in a low alloy content in a high-silicon austenitic stainless steel that maintains a corrosion rate that is comparable to and exceeds those of existing alloys when treating concentrated sulfuric acid. Acceptable characteristics are found when hot working is carried out in the range of about 2,100°F (1,148.9°C) to about 2,200°F (1,204.5°C). Annealing in the range of about 1,925°F (1,051.7°C) to about 2,025°F (1,107.2°C) is preferred, and rapid water quenching after annealing is also preferred.
COPYRIGHT: (C)2008,JPO&INPIT

Abstract translation: 要解决的问题：提供在浓硫酸环境中具有耐腐蚀性的奥氏体不锈钢。 解决方案：奥氏体不锈钢是一种合金，其组成包括重量约为0.025％或更少的碳，约0.5至4.1％的锰，约5.5至约6.2％的硅，约11至约15％的铬 ，约9.0至约15.5％的镍，约0.8至约1.2％的钼，约0.8至约2％的铜，余量基本上为铁和不可避免的杂质。 该组合物在高硅奥氏体不锈钢中导致低合金含量，其在处理浓硫酸时保持与现有合金相当并超过其的腐蚀速率。 在约2,100°F（1,148.9℃）至约2,200°F（1,204.5℃）的范围内进行热加工时，可以发现可接受的特性。 在约1,925°F（1,051.7℃）至约2,025°F（1,107.2℃）的范围内的退火是优选的，并且退火后的快速水淬还是优选的。 版权所有（C）2008，JPO＆INPIT

公开(公告)号：CA2355109A1

公开(公告)日：2000-06-22

申请号：CA2355109

申请日：1999-12-13

Applicant: ATI PROPERTIES INC

Inventor： SORACE DOMINIC A ,  GRUBB JOHN F

IPC: C21D8/02 ,  C22C38/00 ,  C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L29/08 ,  C22C38/34

Abstract: An alloy having a composition, by weight, of about 0.025 % or less carbon, about 0.5 to about 4.1 % manganese, about 5.5 to about 6.2 % silicon, about 11 to about 15 % chromium, about 9.0 to about 15.5 % nickel, about 0.8 to about 1.2 % molybdenum and about 0.8 to about 2 % copper and the remainder being essentially iron with incidental impurities. This composition results in lea n alloy content in a high silicon austenitic stainless steel for concentrated sulfuric acid service while maintaining a corrosion rate similar to and competitive with existing alloys for such service. Acceptable characteristic s were found when hot working was carried out in the range of about 2100 ~F to about 2200 ~F. Annealing in the range of about 1925 ~F to about 2025 ~F is preferred, as is rapid water quenching after annealing.

公开(公告)号：AU2179100A

公开(公告)日：2000-07-03

申请号：AU2179100

申请日：1999-12-13

Applicant: ATI PROPERTIES INC

Inventor： SORACE DOMINIC A ,  GRUBB JOHN F

IPC: C21D8/02 ,  C22C38/00 ,  C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L29/08 ,  C22C38/34

Abstract: An alloy having a composition, by weight, of about 0.025% or less carbon, about 0.5 to about 4.1% manganese, about 5.5 to about 6.2% silicon, about 11 to about 15% chromium, about 9.0 to about 15.5% nickel, about 0.8 to about 1.2% molybdenum and about 0.8 to about 2% copper and the remainder being essentially iron with incidental impurities. This composition results in lean alloy content in a high silicon austenitic stainless steel for concentrated sulfuric acid service while maintaining a corrosion rate similar to and competitive with existing alloys for such service. Acceptable characteristics were found when hot working was carried out in the range of about 2100 DEG F. to about 2200 DEG F. Annealing in the range of about 1925 DEG F. to about 2025 DEG F. is preferred, as is rapid water quenching after annealing.

公开(公告)号：CA2355109C

公开(公告)日：2009-09-22

申请号：CA2355109

申请日：1999-12-13

Applicant: ATI PROPERTIES INC

Inventor： SORACE DOMINIC A ,  GRUBB JOHN F

IPC: C21D8/02 ,  C22C38/44 ,  C22C38/00 ,  C22C38/02 ,  C22C38/34 ,  C22C38/42 ,  C22C38/58 ,  H04L29/08

Abstract: An alloy having a composition, by weight, of about 0.025 % or less carbon, about 0.5 to about 4.1 % manganese, about 5.5 to about 6.2 % silicon, about 11 to about 15 % chromium, about 9.0 to about 15.5 % nickel, about 0.8 to about 1.2 % molybdenum and about 0.8 to about 2 % copper and the remainder being essentially iron with incidental impurities. This composition results in lean alloy content in a high silicon austenitic stainless steel for concentrated sulfuric acid service while maintaining a corrosion rate similar to and competitive with existing alloys for such service. Acceptable characteristics were found when hot working was carried out in the range of about 2100 .degree.F to about 2200 .degree.F. Annealing in the range of about 1925 .degree.F to about 2025 .degree.F is preferred, as is rapid water quenching after annealing.

公开(公告)号：AU765419B2

公开(公告)日：2003-09-18

申请号：AU2179100

申请日：1999-12-13

Applicant: ATI PROPERTIES INC

Inventor： SORACE DOMINIC A ,  GRUBB JOHN F

IPC: C21D8/02 ,  C22C38/00 ,  C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L29/08 ,  C22C38/34

Abstract: An alloy having a composition, by weight, of about 0.025% or less carbon, about 0.5 to about 4.1% manganese, about 5.5 to about 6.2% silicon, about 11 to about 15% chromium, about 9.0 to about 15.5% nickel, about 0.8 to about 1.2% molybdenum and about 0.8 to about 2% copper and the remainder being essentially iron with incidental impurities. This composition results in lean alloy content in a high silicon austenitic stainless steel for concentrated sulfuric acid service while maintaining a corrosion rate similar to and competitive with existing alloys for such service. Acceptable characteristics were found when hot working was carried out in the range of about 2100 DEG F. to about 2200 DEG F. Annealing in the range of about 1925 DEG F. to about 2025 DEG F. is preferred, as is rapid water quenching after annealing.

公开(公告)号：EP1141432A4

公开(公告)日：2002-06-05

申请号：EP99966186

申请日：1999-12-13

Applicant: ATI PROPERTIES INC

Inventor： SORACE DOMINIC A ,  GRUBB JOHN F

IPC: C21D8/02 ,  C22C38/00 ,  C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L29/08 ,  C22C38/34

CPC classification number: C22C38/02 ,  C22C38/42 ,  C22C38/44 ,  C22C38/58 ,  H04L67/02 ,  Y10S707/959 ,  Y10S707/99945

Abstract: An alloy having a composition, by weight, of about 0.025 % or less carbon, about 0.5 to about 4.1 % manganese, about 5.5 to about 6.2 % silicon, about 11 to about 15 % chromium, about 9.0 to about 15.5 % nickel, about 0.8 to about 1.2 % molybdenum and about 0.8 to about 2 % copper and the remainder being essentially iron with incidental impurities. This composition results in lean alloy content in a high silicon austenitic stainless steel for concentrated sulfuric acid service while maintaining a corrosion rate similar to and competitive with existing alloys for such service. Acceptable characteristics were found when hot working was carried out in the range of about 2100 DEG F to about 2200 DEG F. Annealing in the range of about 1925 DEG F to about 2025 DEG F is preferred, as is rapid water quenching after annealing.

Abstract translation: 提供了收集和传送信息的方法。 该方法在包括具有CPU和存储设备的用户计算机的客户端/服务器计算机网络中执行，其适于实现能够从用户的CPU和存储设备收集使用信息的第一客户端程序和提供 与网络的连接。 网络还包括具有能够将可发送文件写入用户计算机的服务器程序的主服务器站点。 至少包含一个第三方服务器站点，并且能够从用户计算机上传可传输的文件。 在第一步中，服务器程序将至少一个可发送文件写入用户计算机。 接下来，第一客户端程序从用户计算机收集使用信息，然后将使用信息写入至少一个可发送文件。 接下来，第一客户端程序将至少一个可发送文件寻址到第三方服务器，并且第二客户端程序将其发送到第三方服务器。 还提供了一种用于在客户/服务器计算机网络中收集和传送信息的装置。 [该装置包括用户计算机，其包括用于从用户的CPU和存储设备收集使用信息的第一客户端程序，用于将使用信息和地址数据写入到至少一个可发送文件，以及第二客户端程序，用于提供与 网络。 该装置还包括主服务器站点，其包括用于将可传输文件写入用户计算机并用于提供与网络的连接的服务器程序。 还提供了至少一个第三方服务器站点。 至少一个第三方站点包括用于从用户计算机上传可传输文件并提供与网络的连接的通信程序。