公开(公告)号：KR1020020096521A

公开(公告)日：2002-12-31

申请号：KR1020010035081

申请日：2001-06-20

Applicant: 재단법인서울대학교산학협력재단

Inventor： 홍국선 ,  유현승 ,  이동호 ,  이춘기 ,  장봉순 ,  김진호 ,  정성수 ,  윤혁준

IPC: A61L27/10

Abstract: PURPOSE: A process of preparing a ceramic composite for easy control of biosolubility by improving sinterability of a hydroxyapatite and tricalcium phosphate complex is provided which increases strength of the ceramic composite by 3 times while obtaining high density ceramic. Thus obtained ceramic composite can be applied to an artificial tooth and bone-graft material. CONSTITUTION: About 0.2 to 10% by weight of a magnesium salt is added to a complex of hydroxyapatite and tricalcium phosphate in a ratio of 5:95 to 80:20. The magnesium salt comprises one or more selected from the group consisting of magnesium nitrate, magnesium chloride, magnesium oxide, magnesium hydroxide and magnesium carbonate. In a case of synthesizing the hydroxyapatite and tricalcium phosphate, a magnesium is added instead of a calcium salt and then sintered.

Abstract translation: 目的：提供一种通过提高羟基磷灰石和磷酸三钙复合物的烧结性来控制生物溶解性的陶瓷复合材料的制备方法，其在获得高密度陶瓷的同时提高陶瓷复合材料的强度3倍。 这样获得的陶瓷复合材料可以应用于人造牙和骨移植材料。 构成：将约0.2〜10重量％的镁盐以5:95〜80:20的比例加入到羟基磷灰石和磷酸三钙的配合物中。 镁盐包括选自硝酸镁，氯化镁，氧化镁，氢氧化镁和碳酸镁的一种或多种。 在合成羟基磷灰石和磷酸三钙的情况下，加入镁代替钙盐，然后烧结。

公开(公告)号：KR100583849B1

公开(公告)日：2006-05-26

申请号：KR1020040004087

申请日：2004-01-20

Applicant: 재단법인서울대학교산학협력재단

Inventor： 유현승 ,  이동수 ,  홍국선 ,  이춘기 ,  이재협 ,  이동호 ,  장봉순 ,  김진영 ,  정성수

IPC: C04B35/447

CPC classification number: A61L27/32 ,  A61K33/42 ,  A61L27/12 ,  A61K2300/00

Abstract: 본 발명은 졸-겔법을 이용하여 칼슘과 인산 성분이 완전히 녹아있어 투명하고 균일하며 젖음성과 생체활성이 우수한 아파타이트를 포함한 인산칼슘 화합물의 폴리메릭 졸을 합성하고 이것을 금속 이식체에 코팅한 후 열처리함으로써 기판과의 부착강도가 높고 치밀하게 소결된 코팅층을 형성할 수 있는 인산칼슘 화합물의 폴리메릭 졸 제조방법과 그의 금속 이식체 코팅방법에 관한 것이다.
상기 폴리메릭 졸은 각각 유기산에 칼슘에톡사이드를 녹인 칼슘염 용액과, 유기산에 트리에틸포스파이트 또는 트리에틸포스페이트를 녹인 인산염 용액을 준비한 후, 상기 칼슘염 용액과 인산염 용액을 혼합한 후 혼합 용액을 숙성시켜서 얻어진다. 또한, 상기 폴리메릭 졸을 금속 이식체의 표면에 코팅하고, 금속 이식체의 코팅막을 가수분해한 후, 상기 코팅막을 예비 열처리하여 코팅막에 남아있는 유기물을 태워버리는 과정을 반복하여 상기 코팅막을 원하는 두께로 증가시킨 후, 상기 금속 이식체를 질소 분위기 하에서 500℃~800℃의 온도에서 소결함에 의해 금속 이식체에 대한 코팅막을 형성할 수 있다.
인산칼슘 세라믹, 금속 이식체 코팅, 졸-겔법, 젖음성, 균일 코팅

公开(公告)号：KR100484892B1

公开(公告)日：2005-04-28

申请号：KR1020020051243

申请日：2002-08-28

Applicant: 재단법인서울대학교산학협력재단

Inventor： 유현승 ,  홍국선 ,  김환 ,  이동호 ,  이춘기 ,  장봉순 ,  김득중 ,  서준혁 ,  이재협 ,  박기수

IPC: C04B38/00 ,  C03C10/04 ,  A61L27/00

CPC classification number: C03C11/00

Abstract: 본 발명은 조성 중에 고온에서 가스를 발생하는 성분을 포함한 유리로서 이를 분쇄한 후 열처리시 치밀하게 소결된 후 급격히 발포되어 높은 기공율을 가지나 강도가 매우 높은 자가 발포형 다공성 세라믹 조성물 및 이를 이용한 다공성 세라믹의 제조방법에 관한 것이다.
본 발명의 자가발포형 다공성 세라믹 조성물은 각각 몰비로 산화칼슘(CaO)이 43∼47%, 실리카(SiO
2 )가 43∼47%, 보레이트(B
2 O
3 )가 6∼14% 범위 안에서 조성되는 것을 특징으로 한다.
상기 다공성 세라믹은 CaO, SiO
2 및 B
2 O
3 로 구성된 유리를 제조하는 단계와; 이 유리를 평균입경 1∼10μm 범위의 미세한 분말로 분쇄하는 단계와; 상기 분말을 프레스로 성형하는 단계와; 상기 성형물을 950~1200℃ 사이의 온도에서 열처리하여 자가발포시키는 단계를 포함하는 것을 특징으로 제조공정에 따라 얻어진다.

公开(公告)号：KR100460685B1

公开(公告)日：2004-12-09

申请号：KR1020020019520

申请日：2002-04-10

Applicant: 재단법인서울대학교산학협력재단

Inventor： 유현승 ,  홍국선 ,  이춘기 ,  이동호 ,  이상림 ,  장봉순 ,  김수진 ,  임창균

IPC: A61L27/12

CPC classification number: A61L27/12 ,  A61F2/4644 ,  A61F2002/2835 ,  A61F2310/00293 ,  A61L27/56 ,  A61L2430/02

Abstract: A bone graft substitute using magnesium substituted calcium phosphate compounds and a method of manufacturing the same is provided in which the bone graft substitute is used for recovering bones damaged due to a bone fracture. The method of manufacturing a bone graft substitute includes the steps of mixing powdered calcium pyrophosphate and a magnesium included compound to thereby obtain a composition, pressure-forming the compositions to obtain a plastic body; and sintering the plastic body.

Abstract translation: 提供了使用镁取代磷酸钙化合物的骨移植替代物及其制造方法，其中骨移植替代物用于恢复由于骨折而损坏的骨。 制造骨移植替代品的方法包括以下步骤：将粉状焦磷酸钙和含镁化合物混合，从而获得组合物，将组合物加压成形以获得塑性体; 并烧结塑料体。

公开(公告)号：KR1020040021111A

公开(公告)日：2004-03-10

申请号：KR1020020052566

申请日：2002-09-02

Applicant: 재단법인서울대학교산학협력재단

Inventor： 유현승 ,  홍국선 ,  김환 ,  이동호 ,  이춘기 ,  장봉순 ,  김득중 ,  서준혁 ,  이재협 ,  박기수

IPC: A61L27/10

CPC classification number: C03C4/0007 ,  A61L27/10 ,  A61L27/58 ,  C03C3/064 ,  C03C3/112 ,  C03C4/0014 ,  C03C8/22 ,  C03C10/00 ,  C03C11/00 ,  C03C12/00

Abstract: PURPOSE: A bioabsorbable type bioactive glass-ceramic and a preparation method thereof are provided to control the biodegradable speed according to the formulation ratio of glass-ceramics while maintaining the bioactivity. CONSTITUTION: The bioabsorbable type bioactive glass-ceramic comprises 41.4 to 45.75 wt.% of CaO, 35.0 to 47.62 wt.% of SiO2, 1.62 to 14.58 wt.% of P2O5, 0.5 to 14.58 wt.% of B2O3, 0.46 to 4.14 wt.% of MgO, and 0.05 to 0.45 wt.% of CaF2. The bioabsorbable type bioactive glass-ceramic is composed of the first glass and the second glass in a weight ratio of 90:10 to 10:90. The first glass comprises 41.03 to 45.86 wt.% of CaO, 43.97 to 49.14 wt.% of SiO2, and 5 to 15 wt.% of B2O3. The second glass comprises 44.7 wt.% of CaO, 44.7 wt.% of MgO, 34.0 wt.% of SiO2, 16.2 wt.% of P2O5, and 0.5 wt.% of CaF2.

Abstract translation: 目的：提供生物可吸收型生物活性玻璃陶瓷及其制备方法，以在保持生物活性的同时，根据玻璃陶瓷配方比例控制生物降解速度。 构成：生物可吸收型生物活性玻璃 - 陶瓷包含41.4〜45.75重量％的CaO，35.0〜47.62重量％的SiO 2，1.62〜14.58重量％的P 2 O 5，0.5〜14.58重量％的B 2 O 3，0.46〜4.14重量％ 的MgO，0.05〜0.45重量％的CaF 2。 生物可吸收型生物活性玻璃陶瓷由第一玻璃和第二玻璃组成，重量比为90:10至10:90。 第一玻璃包含CaO的41.03〜45.86重量％，SiO 2为43.97〜49.14重量％，B 2 O 3为5〜15重量％。 第二种玻璃包括44.7wt％的CaO，44.7wt％的MgO，34.0wt。％的SiO 2，16.2wt。％的P 2 O 5和0.5wt％的CaF 2。

公开(公告)号：KR1020040011885A

公开(公告)日：2004-02-11

申请号：KR1020020045175

申请日：2002-07-31

Applicant: 재단법인서울대학교산학협력재단

Inventor： 유현승 ,  홍국선 ,  이춘기 ,  이동호 ,  이재협 ,  장봉순 ,  김수진 ,  정성수

IPC: A61L27/10

Abstract: PURPOSE: Provided are a bio-active ceramics and a metallic implant used in surgical and dental applications coated with the ceramics in order to increase bio-affinity to a subject having the implant. CONSTITUTION: The bio-active ceramics comprises 40-49 wt.% of CaO, 40-49 wt.% of silica(SiO2) and 2-20 wt.% of B2O3. The process for producing the metallic implant comprises steps of preparing the bio-active ceramic by fusing raw material consisting of CaO, SiO2, B2O3 and quenching the fused material; grinding the frozen material into powders having less than 10 micrometer size; preparing slurry by adding aqueous or organic solvents and a binder; applying the slurry to a metallic implant by means of brush; and sintering the coated implant at 700-950 deg.C.

Abstract translation: 目的：提供一种生物活性陶瓷和用于外科和牙科应用的金属植入物，其涂覆有陶瓷，以增加对具有植入物的受试者的生物亲和力。 构成：生物活性陶瓷包含40-49重量％的CaO，40-49重量％的二氧化硅（SiO 2）和2-20重量％的B 2 O 3。 制造金属植入体的方法包括以下步骤：通过熔融由CaO，SiO 2，B 2 O 3组成的原料和淬火熔融材料来制备生物活性陶瓷; 将冷冻材料研磨成具有小于10微米尺寸的粉末; 通过加入水或有机溶剂和粘合剂制备浆料; 通过刷子将浆料施加到金属植入物; 并在700-950℃烧结涂覆的植入物。