公开(公告)号：KR1020070113693A

公开(公告)日：2007-11-29

申请号：KR1020060047276

申请日：2006-05-25

Applicant: 현대자동차주식회사

Inventor： 이춘수

IPC: B29B9/06 ,  B29B9/14

CPC classification number: B29B9/06 ,  B29B9/14 ,  B29C70/06

Abstract: A method for preparing poly lactic acid-natural fibers composites is provided to produce the poly lactic acid-natural fibers composites having excellent mechanical physical properties such as impact strength, tensile strength and flexural modulus and showing extrusion moldability. A method for preparing poly lactic acid-natural fibers composites comprises the steps of: washing natural fibers with a detergent for 1-24 hours; drying the natural fibers at 30-100 deg.C for 6-72 hours; drying poly lactic acid and the natural fibers for 1-12 hours and then compounding the dried poly lactic and natural fibers in a weight ratio of 1:0.2-1.5 by using an extruder under 170-220 deg.C and a screw rotary speed of 30-500 rpm; and cutting the extruded strands into 5-30 mm for pelletization.

Abstract translation: 提供了一种制备聚乳酸 - 天然纤维复合材料的方法，以生产具有优异的机械物理性能如冲击强度，拉伸强度和弯曲模量并显示挤出成型性的聚乳酸 - 天然纤维复合材料。 制备聚乳酸 - 天然纤维复合材料的方法包括以下步骤：用洗涤剂洗涤天然纤维1-24小时; 将天然纤维在30-100℃干燥6-72小时; 干燥聚乳酸和天然纤维1-12小时，然后通过使用挤出机在170-220℃下以1:0.2-1.5的重量比混合干燥的聚乳酸和天然纤维，并将螺杆转速 30-500 rpm; 并将挤出的股线切割成5-30mm以进行造粒。

公开(公告)号：KR1020070054470A

公开(公告)日：2007-05-29

申请号：KR1020050112492

申请日：2005-11-23

Applicant: 현대자동차주식회사

Inventor： 이춘수 ,  조재영 ,  남병욱 ,  배진우

IPC: C08K9/06 ,  B82B3/00 ,  B82B1/00

CPC classification number: C08K9/04 ,  B82B1/00 ,  B82Y30/00 ,  C08J3/22 ,  C08K3/346 ,  C08K5/14 ,  C08L23/06 ,  C08L23/12

Abstract: 본 발명은 폴리올레핀／클레이 나노복합재 및 이의 제조방법에 관한 것으로서, 더욱 상세하게는 감마선이 조사된 유기화된 클레이, 폴리올레핀 및 라디칼 개시제를 컴파운딩하여, 상기 유기화된 클레이를 감마선을 조사하여 형성된 라디칼과 폴리올레핀이 라디칼 개시제에 의해 형성된 라디칼이 공유결합하여 제조된 나노복합재는 종래 상용화제의 사용 없이 골고루 분산될 뿐만 아니라 상용화제에 의한 물성 저하 문제를 개선하면서 동시에 클레이의 박리가 효과적으로 수행되는 폴리올레핀／클레이 나노복합재 및 이의 제조방법에 관한 것이다.
폴리올레핀, 클레이, 나노복합재, 감마선, 개질, 공유결합, 분산

公开(公告)号：KR1020070034853A

公开(公告)日：2007-03-29

申请号：KR1020050089460

申请日：2005-09-26

Applicant: 현대자동차주식회사

Inventor： 이춘수 ,  조재영 ,  이용범 ,  배진우 ,  남병욱

IPC: B82B3/00 ,  B82Y40/00

CPC classification number: C08K3/346 ,  C08K2201/011 ,  C08L23/12 ,  C08L51/06

Abstract: 본 발명은 폴리프로필렌/클레이 나노복합재의 제조방법에 관한 것으로서, 더욱 상세하게는 아미노 실란으로 개질한 기능성 클레이를 폴리프로필렌 및 상용화제인 무수 말레인산이 그래프트된 폴리프로필렌과 함께 용융 혼합하는 방법으로, 기능성 클레이 표면에 무수 말레인산이 그래프트된 폴리프로필렌을 공유결합시켜 클레이를 폴리프로필렌 매트릭스에 효과적으로 분산시키는 새로운 나노복합재의 제조방법에 관한 것이다.

폴리프로필렌, 클레이, 나노복합재, 아미노 실란, 개질, 무수 말레인산이 그래프트된 폴리프로필렌, 공유결합, 분산

Abstract translation: 本发明是一个聚丙烯/作为粘土涉及一种方法，用于制造纳米复合材料，并且更具体地涉及用氨基硅烷如聚丙烯和相容剂的马来酸酐接枝聚丙烯，官能粘土改性熔体与官能粘土混合的方法 通过共价键，以马来酸酐接枝的聚丙烯的制造新的纳米复合材料，以有效地分散在聚丙烯基质中的粘土的方法的表面上。

公开(公告)号：KR101500004B1

公开(公告)日：2015-03-09

申请号：KR1020090097779

申请日：2009-10-14

Applicant: 현대자동차주식회사 ,  주식회사 엘지화학

Inventor： 이춘수 ,  이민희 ,  이주형 ,  최기대

IPC: C08L77/02 ,  C08L23/00 ,  C08L51/06 ,  C08K3/00

Abstract: 본 발명은 자동차 연료튜브 외층용 폴리아마이드/폴리올레핀/나노클레이 복합재에 관한 것으로서, 더욱 상세하게 설명하면, 폴리아마이드 수지와 폴리올레핀 수지를 함유한 주재, 충격보강제, 무기필러 등을 포함하는 복합재에 관한 것이다. 본 발명의 상기 복합재는 내연료투과성이 우수하기 때문에 자동차 연료시스템, 특히 연료튜브로 사용하기에 적합하며, 저가의 폴리올레핀 소재를 사용으로 인한 원가 절감 효과가 있기 때문에 경제성이 우수하다.
나노복합재, 내연료투과성, 폴리아마이드, 폴리올레핀, 클레이, 연료튜브

公开(公告)号：KR101293916B1

公开(公告)日：2013-08-08

申请号：KR1020110092198

申请日：2011-09-09

Applicant: 현대자동차주식회사 ,  주식회사 효성 ,  주식회사 데스코

Inventor： 이춘수 ,  이민희 ,  박봉현 ,  김종활 ,  윤성균 ,  강병국 ,  이근규 ,  이종

IPC: C08L67/04 ,  C08L73/00 ,  C08L15/00 ,  C08L61/02

CPC classification number: C08L67/04 ,  C08L21/00 ,  C08L73/00

Abstract: 본 발명은 내열성 및 내충격성이 향상된 폴리유산 조성물에 관한 것으로서, 보다 구체적으로는 폴리케톤 및 변성 고무를 혼합함으로써 충격강도와 내열성이 동시에 향상된 폴리유산 조성물에 관한 것이다.
본 발명에 따른 폴리유산 조성물은 내열성, 내화학성, 내연료투과성, 내마모성 등이 우수한 동시에 내충격성과 내열성을 향상시킴으로써 바이오플라스틱인 폴리유산을 자동차용 내외장 부품에 사용할 수 있다.

公开(公告)号：KR1020130028560A

公开(公告)日：2013-03-19

申请号：KR1020110092200

申请日：2011-09-09

Applicant: 현대자동차주식회사 ,  주식회사 효성

Inventor： 이춘수 ,  윤지용 ,  윤성균 ,  강병국 ,  이종

IPC: C08K5/17 ,  C08L73/00 ,  C08C19/28 ,  B60R13/00

CPC classification number: C08K5/17 ,  B60R13/00 ,  C08C19/28 ,  C08L73/00 ,  C08L2201/02

Abstract: PURPOSE: A polyketone composition is provided to improve impact resistance and flexability and to have excellent chemical resistance, anti-fuel permeability, heat resistance, and abrasion resistance. CONSTITUTION: A polyketone composition comprises 0.01-0.5 parts by weight of an amine crosslinking agent and 100.0 parts by weight of polyketone. The polyketone is a homopolymer or alloy of a polyketone and modified rubber. The content of the modified rubber in the alloy of the polyketone and the modified rubber is 1-50%/ The modified rubber is modified by a maleic anhydride or glycidyl group. The amine crosslinking agent is diamine or triamine. [Reference numerals] (AA,CC) Polyketone; (BB) Diamine; (DD) Imine bond

Abstract translation: 目的：提供聚酮组合物以改善耐冲击性和挠曲性，并且具有优异的耐化学性，抗燃料渗透性，耐热性和耐磨性。 构成：聚酮组合物包含0.01-0.5重量份的胺交联剂和100.0重量份的聚酮。 聚酮是聚酮和改性橡胶的均聚物或合金。 聚酮和改性橡胶合金中改性橡胶的含量为1-50％/改性橡胶用马来酸酐或缩水甘油基改性。 胺交联剂是二胺或三胺。 （AA，CC）聚酮; （BB）二胺; （DD）亚胺键

公开(公告)号：KR101144110B1

公开(公告)日：2012-05-24

申请号：KR1020090117214

申请日：2009-11-30

Applicant: 현대자동차주식회사 ,  기아자동차주식회사 ,  롯데케미칼 주식회사

Inventor： 이춘수 ,  이민희 ,  고성록 ,  남병국 ,  김세훈

IPC: C08K3/00 ,  C08K7/28 ,  C08L23/12 ,  C08J3/22

CPC classification number: C08K3/40 ,  C08K3/346 ,  C08K7/28 ,  C08K2201/011 ,  C08L23/06 ,  C08L23/0815 ,  C08L23/10 ,  C08L23/142 ,  C08L23/16 ,  C08L23/20 ,  C08L2666/02

Abstract: Thermoplastic polyolefin (TPO)-nanocomposite material composition comprises polypropylene resin, polyethylene resin, gum resin, nanoclay masterbatch and glass bubbles master batch. An independent claim is also included for producing TPO-composite material, comprising introducing the glass bubbles masterbatch by a lateral inlet.

公开(公告)号：KR1020120005256A

公开(公告)日：2012-01-16

申请号：KR1020100065903

申请日：2010-07-08

Applicant: 현대자동차주식회사

Inventor： 이춘수 ,  이민희

IPC: C08L23/10 ,  C08L23/16 ,  C08K3/22 ,  C08K9/06

CPC classification number: C08L23/10 ,  C08K3/04 ,  C08K3/08 ,  C08K5/54 ,  C08K7/24 ,  C08K9/06 ,  C08K2003/2241 ,  C08K2003/2296 ,  C08K2201/011 ,  C08L23/16

Abstract: PURPOSE: A polypropylene resin composition is provided to offer high glossy surface property of the black color to interior and external parts of vehicles by an extruding process of polypropylene. CONSTITUTION: A polypropylene resin composition contains 90-99.8wt% of polypropylene or a polypropylene/rubber mixture having the transparency of 10~90%, 0.2-10wt% of metal oxide nanopowder, and 100-5,000ppm of black coloring agent. The polypropylene is selected from the following: a propylene homopolymer; a random copolymer obtained by copolymerizing 80-90mol% of propylene monomer with 10-20mol% of co-monomer of ethylene, 1-butene, 1-hexene, 1-octene, or 4-methyl-1-pentene; and a block copolymer obtained by blending 1-10wt% of ethylene-propylene rubber to 90-99wt% of homopolymer.

Abstract translation: 目的：提供聚丙烯树脂组合物，通过聚丙烯的挤出方法为车辆的内部和外部部件提供黑色的高光泽表面性能。 构成：聚丙烯树脂组合物含有90-99.8wt％的聚丙烯或透明度为10〜90％，金属氧化物纳米粉末为0.2-10wt％，黑色着色剂为100-5,000ppm的聚丙烯/橡胶混合物。 聚丙烯选自以下：丙烯均聚物; 通过使80-90mol％的丙烯单体与10-20mol％的乙烯，1-丁烯，1-己烯，1-辛烯或4-甲基-1-戊烯的共聚单体共聚得到的无规共聚物; 和通过将1-10重量％的乙烯 - 丙烯橡胶与90-99重量％的均聚物共混获得的嵌段共聚物。

公开(公告)号：KR101047408B1

公开(公告)日：2011-07-08

申请号：KR1020080120141

申请日：2008-11-28

Applicant: 현대자동차주식회사

Inventor： 박충섭 ,  이춘수 ,  정우철 ,  김윤석

IPC: B05D5/00

Abstract: 본 발명은 다중 입체패턴 형성을 위한 자기도장방법에 관한 것으로, 더욱 상세하게는 자성 안료를 포함하는 도료를 특정 패턴을 갖는 외부 자기장에 반응시켜 3차원 입체패턴을 구현하되 시야각에 따라 다른 패턴의 3차원 무늬가 보이도록 하는 다중 입체패턴 형성을 위한 자기도장방법에 관한 것이다.
이를 위하여 본 발명은 (a) 백킹시트 표면에 자성 안료를 포함하는 도료를 도포하여 패턴층을 형성하는 단계; (b) 상기 패턴층을 입체패턴으로 형성한 외부 자기장에 반응시켜 패턴층 내에 자성 안료가 외부 자기장에 의해 배열되어 입체패턴을 형성하는 단계; (c) 상기 (b)단계의 패턴층에 500~1000mJ/㎠의 자외선을 1~5분 동안 조사하여 부분 경화하는 단계; (d) 상기 (c)단계의 패턴층을 60~90℃에서 1~10분 동안 예열하여 경화하는 단계; (e) 상기 (d)단계의 패턴층에 60~90℃에서 1~10분 동안 예열된 투명필름을 적층하여 열접착하는 단계; (f) 상기 투명필름과 패턴층을 압착 및 냉각하고 상기 백킹시트에서 분리시켜 필름을 마련하는 단계;를 포함하여 이루어지며, 상기 (a) ~ (f)단계를 2회 이상 반복하되, 상기 (b)단계에서 외부 자기장의 중심축이 패턴층의 표면에 대해 매회(每回)마다 다른 각도의 기울기를 갖도록 형성하고, 전회(前回)의 (f)단계에서 마련한 필름을 다음 회의 (e)단계에서 패턴층에 열접착하는 필름(투명필름)으로 사용하는 것을 특징으로 하는 다중 입체패턴 형성을 위한 자기도장방법을 제공한다.
자성 안료, 자기장, 패턴층, 다중 입체패턴, 시야각

公开(公告)号：KR1020110060592A

公开(公告)日：2011-06-08

申请号：KR1020090117214

申请日：2009-11-30

Applicant: 현대자동차주식회사 ,  기아자동차주식회사 ,  롯데케미칼 주식회사

Inventor： 이춘수 ,  이민희 ,  고성록 ,  남병국 ,  김세훈

IPC: C08K3/00 ,  C08K7/28 ,  C08L23/12 ,  C08J3/22

CPC classification number: C08K3/40 ,  C08K3/346 ,  C08K7/28 ,  C08K2201/011 ,  C08L23/06 ,  C08L23/0815 ,  C08L23/10 ,  C08L23/142 ,  C08L23/16 ,  C08L23/20 ,  C08L2666/02

Abstract: PURPOSE: A TPO nanocomposite composition is provided to ensure low specific gravity, gloss reduction effect, and excellent scratch resistance since nanoclay and glass bubble are usded. CONSTITUTION: A TPO nanocomposite composition comprises 30~60 weight% of a polypropylene resin, 1~10 weight% of a polyethylene resin, 10~40 weight% of rubber resin, 4~20 weight% of nanoclay masterbatch and 10~30 weight% of glass bubble master batch. The average molecular weight of polypropylene resin is 50,000 ~ 300,000. The polypropylene resin is one selected from polypropylene, polyethylene-propylene copolymer, and polypropylene-butadiene copolymer.

Abstract translation: 目的：提供TPO纳米复合材料组合物，以确保低比重，光泽降低效果和优异的耐擦伤性，因为纳米粘土和玻璃泡被使用。 构成：TPO纳米复合材料组合物包含30-60重量％的聚丙烯树脂，1〜10重量％的聚乙烯树脂，10〜40重量％的橡胶树脂，4〜20重量％的纳米粘土母料和10〜30重量％ 的玻璃泡母料。 聚丙烯树脂的平均分子量为50,000〜30万。 聚丙烯树脂是选自聚丙烯，聚乙烯 - 丙烯共聚物和聚丙烯 - 丁二烯共聚物中的一种。