Abstract: By polymerizing acrylonitrile, AlBN with a DMSO solvent, a polymer is produced which is removed of the foam and a spinning undiluted fluid is produced. The solidified yarn produced is washed and is drawn in the three stage temperature water tub 40, 60, 95 degree C, to 5 times length. In the 1st stage drawing, silicon emulsifying agent is added, transferred to the drying part, and the silicon emulsifying agent is given, transferred to the 2nd drying part where the temperature is 150 degree C, and moved to the 180 degree C hot dir drawing part, where it is drawn by the roller range of 1.5-3g/d and the fine acrylic fiber for reinforcement is produced.
Abstract translation: 通过用DMSO溶剂聚合丙烯腈，AlBN，产生聚合物，其被除去泡沫并产生纺丝未稀释的流体。 将生产的固化纱线洗涤并在三级温水浴缸中40℃，60℃，95℃下拉至5次。 在第一阶段拉伸中，加入硅乳化剂，转移到干燥部分，并给出硅乳化剂，转移到温度为150摄氏度的第二干燥部分，并移动到180℃热拉伸 部分，其中由1.5-3g / d的辊范围拉伸，并且生产用于增强的精细丙烯酸纤维。
-
公开(公告)号：KR1019960034493A
公开(公告)日：1996-10-22
申请号：KR1019950005930
申请日：1995-03-21
Applicant: 한국과학기술연구원
Abstract: 본 발명은 인장 강도 13g/d 및 탄성률 200g/d 이상을 갖고, 장시간 경과후에도 변형률이 3%미만인 시멘트 보강용 고강도 고탄성 아크릴 섬유의 제조 방법에 관한 것이다. 본 발명은, 종래 기술의 1단 건열 연신 방법으로 달성할 수 없는 장시간 경화후 섬유 변형에 따른 문제점을 2단 건열 연신 방법을 사용함으로써 해결하였다. 특히, 본 발명은 2단 건열연신 과정에서 섬유 내부에 응력이 해소됨으로써 섬유의 기계적 성질도 향상시킬 수 있었다.
-
公开(公告)号：KR100124997B1
公开(公告)日：1997-12-15
申请号：KR1019950005930
申请日：1995-03-21
Applicant: 한국과학기술연구원
Abstract: In case the first drawing temp is under 17 degree C, the effective drawing is difficult caused by the lack of drawing heat, while higher than 200 degree C, by the heat movement increase of molecular chain, not only difficult the effective orientation is, but is yellowed, so the temperature is kept to 170-200 degree C for drawing. In case the drawing tension is less than 1g/d, the effective drawing of the fiber is hard, and while higher than 3g/d, the fiber may be curved, accordingly the temperature is limited to 2.5g/d.
Abstract translation: 在第一次拉伸温度低于17℃的情况下，由于缺乏拉伸热，而高于200℃，由于分子链的热运动增加，有效拉伸难以有效取向困难，但是 变黄，所以绘图温度保持在170-200摄氏度。 在拉伸张力小于1g / d的情况下，纤维的有效拉伸是困难的，而高于3g / d的纤维可能是弯曲的，因此温度限制在2.5g / d。
-
公开(公告)号：KR1019960034489A
公开(公告)日：1996-10-22
申请号：KR1019950005929
申请日：1995-03-21
Applicant: 한국과학기술연구원
Abstract: 본 발명은 응고욕 내의 가이드에서 걸리는 필라멘트의 장력을 최소화함으로써 기계적 성질이 우수하고 굵기가 가는 보강재용 아크릴 섬유의 제조 방법에 관한 것이다. 구체적으로 말하면, 응고욕 내에 한 개의 가이드를 두고서 응고사를 견인각이 90도 미만인 상방향으로 견인하는 종래 기술의 방법과 달리, 본 발명은 응고욕 내에 2개의 가이드를 두고서 제1가이드에서 견인각을 90내지 120도로 하여 제1가이드에 걸리는 장력을 최소화하고, 고속 견인에 따른 장력이 공기층 내의 압출 필라멘트에 전달되도록 함으로써, 굵기가 가늘고 기계적 성질이 우수한 섬유를 제조한다.
-
-
-