公开(公告)号：KR100716069B1
公开(公告)日：2007-05-09
申请号：KR1020050021689
申请日：2005-03-16
Applicant: 한국에너지기술연구원
IPC: C09K11/80
CPC classification number: Y02B20/181
Abstract: 본 발명은 백색 발광 형광체의 제조방법에 관한 것으로, 그 목적은 전계방출소자용 형광체에 적용되는, 화학적 결합이 우수하고, 강한 전류 밀도에도 퇴화되지 않는 산화물 형광체 중에서 천연색을 발광하는 백색 발광 형광체의 제조방법을 제공하는데 있다.
본 발명의 구성은 일반식 ZnGa
2 O
4 :X
m ,Y
n (단, 활성화제 X와 Y에 있어서 X는 Tb
3+ , Mn
2+ 중에서 선택된 하나이고, Y는 Eu
3+ , Cr
3 중에서 선택된 하나로 구성되며, m은 0＜ m≤0.10의 범위이고, n은 0＜ n≤0.10의 범위임)로 표시되어 조성된 백색 발광 형광체의 제조방법을 특징으로 한다.
ZnGa2O4:Xm,Yn, 형광체, 전계발광소자, 백색 광원-
公开(公告)号：KR1020000015266A
公开(公告)日：2000-03-15
申请号：KR1019980035080
申请日：1998-08-28
Applicant: 한국에너지기술연구원
CPC classification number: C01B32/306 , C01B32/33
Abstract: PURPOSE: A preparation method of carbon molecular substance by using volatile organic material is provided which is used in the refinery of ethanol, separating nitrogen from air. CONSTITUTION: Coconut powder is mixed with lignin, coal tar pitch, starch, and vegetable-oil to give cylinder shaped carbon compounds with a diameter of 2mm-3mm, followed by drying at 50-100°C, and carbonated through 3 steps in a rotary carbonating furnace at 100-850°C. In this process, nitrogen and argon gas(0.5-2 liter/min) are supplied in reverse direction into the rotary carbonating furnace to give cylinder shaped carbon compounds.
Abstract translation: 目的：提供使用挥发性有机材料制备碳分子物质的方法，该方法用于乙醇的炼油厂，将氮气与空气分离。 构成：将椰子粉与木质素，煤焦油沥青，淀粉和植物油混合，得到直径为2mm-3mm的圆筒形碳化合物，然后在50-100℃下干燥，并通过3步骤碳酸化 旋转碳酸炉在100-850°C。 在这个过程中，将氮和氩气（0.5-2升/分钟）反向供给到旋转碳酸炉中，得到圆筒形碳化合物。
-
公开(公告)号：KR100748622B1
公开(公告)日：2007-08-10
申请号：KR1020060048977
申请日：2006-05-30
Applicant: 한국에너지기술연구원
Abstract: A method for producing an environment-friendly heat insulating light weight porous board with uniform pores using water glass without a low temperature through control of reaction temperature. A method includes the steps of: mixing sodium silicate comprising 30 to 35 wt% of silicon dioxide(SiO2) and having a viscosity of 600(CP) with calcium phosphate as a catalyst, sodium aluminate(NaAlO2) powder as a pore forming agent, potassium silicate(K2SiO3) aqueous solution comprising 19 wt% of silicon dioxide(SiO2) as a water resistant enhancer and anti-whitening agent in an attrition mill, loading the mixture in a mold, followed by curing at 350 to 500 deg.C. The calcium phosphate is one selected from Ca(H2PO4)2, Ca2(HPO4)2, Ca3(PO4)2 and a mixture thereof and used in an amount of 1 to 2 weight parts based on 100 weight parts of the mixture. The sodium aluminate is used in an amount of 4 to 7 weight parts based on 100 weight parts of the mixture. The potassium silicate(K2SiO3) is used in an amount of 2 to 5 weight parts based on 100 weight parts of the mixture.
Abstract translation: 通过控制反应温度，使用没有低温的水玻璃生产具有均匀孔隙的环保型隔热轻质多孔板的方法。 一种方法包括以下步骤：将包含30-35wt％二氧化硅（SiO 2）且粘度为600（CP）的硅酸钠与作为催化剂的磷酸钙，作为成孔剂的铝酸钠（NaAlO 2）粉末， 硅酸钾（K2SiO3）水溶液，该水溶液在研磨机中包含19重量％的二氧化硅（SiO2）作为耐水增强剂和抗白化剂，将该混合物装入模具中，然后在350至500℃下固化。 磷酸钙是选自Ca（H 2 PO 4）2，Ca 2（HPO 4）2，Ca 3（PO 4）2及其混合物中的一种，并且基于100重量份的混合物，磷酸钙的用量为1至2重量份。 基于100重量份的混合物，铝酸钠的用量为4至7重量份。 基于100重量份的混合物，硅酸钾（K2SiO3）的用量为2至5重量份。
-
公开(公告)号：KR100148205B1
公开(公告)日：1998-08-01
申请号：KR1019950014824
申请日：1995-06-05
Applicant: 한국에너지기술연구원
Abstract: 본 발명은 가열된 폐유내에서 폐타이어를 열분해 반응시켜 오일화하기 위한 열분해 반응조건과 장치 및 그 방법에 관한 것으로 열분해 반응시 온도를 380℃로 낮추고 폐타이어와 폐유의 공급비를 2:1하여 분해시킴으로서 폐유에 대한 폐타이어의 처리량을 높이고 열효율을 증대시켰으며 반응기내 첨가제 수산화 칼슘[Ca(OH)
2 ]을 첨가하여 열분해 생성오일중의 유황분과 염소등의 유해물질의 함유량을 최소화하였고, 열분해 장치의 기계적 결함을 해소하기 위해 폐유가열장치, 폐타이어의 연속공급장치, 열분해 반응기 및 잔유물 건조기의 장치상의 문제점을 개선한 폐타이어/폐유의 복합열분해에 의한 오일화 장치.
-
-
-