公开(公告)号：KR1020100012199A

公开(公告)日：2010-02-08

申请号：KR1020080073461

申请日：2008-07-28

Applicant: (재)울산테크노파크

Inventor： 김영혁 ,  태원필 ,  허대영 ,  남두현 ,  이재신

IPC: C04B35/495 ,  C04B35/453 ,  B82Y30/00

CPC classification number: H01L41/1873 ,  C04B35/495 ,  C04B35/64 ,  C04B2235/40 ,  C04B2235/5445 ,  C04B2235/5454 ,  G01H11/08 ,  H01L41/43

Abstract: PURPOSE: A ceramic composition of lead-free piezoelectric for the ultrasonic sensor is provided to ensure high mechanical quality factor and piezoelectric properties and to realize low-temperature sintering by adding Zn nanopowder in (Na0.5K0.5)NbO3 composition. CONSTITUTION: A ceramic composition of lead-free piezoelectric for the ultrasonic sensor comprises (Na0.5K0.5)NbO3 and 1 ~ 10 mol% of zinc(Zn) nanopowder as an additive. An average particle size of the zinc(Zn)nanopowder is 20 ~ 200nm. A ceramic composition of lead-free piezoelectric is manufactured by setting a sintering temperature to 980 ~ 1060°C and the temperature is lower than the sintering temperature of general PZT powder with 1200°C ~ 1350°C.

Abstract translation: 目的：提供超声波传感器的无铅压电陶瓷组合物，以确保高机械品质因数和压电性能，并通过在（Na0.5K0.5）NbO3组合物中添加Zn纳米粉末实现低温烧结。 构成：用于超声波传感器的无铅压电陶瓷组合物包括（Na0.5K0.5）NbO3和1〜10mol％的锌（Zn）纳米粉末作为添加剂。 锌（Zn）纳米粉末的平均粒径为20〜200nm。 通过将烧结温度设定为980〜1060℃，温度低于1200℃〜1350℃的普通PZT粉末的烧结温度，制造无铅压电陶瓷组合物。

公开(公告)号：KR1020100033002A

公开(公告)日：2010-03-29

申请号：KR1020080091947

申请日：2008-09-19

Applicant: (재)울산테크노파크

Inventor： 김영혁 ,  태원필 ,  허대영 ,  지한나

IPC: H01L41/187 ,  C04B35/495 ,  C04B35/64 ,  A61H23/02

CPC classification number: H01L41/187 ,  A61H23/0245 ,  A61H2201/1207 ,  C04B35/495 ,  C04B35/64

Abstract: PURPOSE: A free-lead piezoelectric ceramic composition for an ultrasonic oscillator is provided to enhance sintering property and to form the free-lead piezoelectric ceramic composition at a low sintering temperature. CONSTITUTION: A free-lead piezoelectric ceramic composition for an ultrasonic oscillator is composed of (Na0.5K0.5)NbO3. An additive which is added to the composition contains 0.1 ~ 3 mol% of metal oxide selected from Fe2O or NiO and 0.1 ~ 3 mol% of metal oxide selected from MnCO3 or CuO. A sintering temperature of the free-lead piezoelectric ceramic composition which is composed of (Na0.5K0.5)NbO3 is 1000 ~ 1075°C.

Abstract translation: 目的：提供一种用于超声波振荡器的自由铅压电陶瓷组合物，以提高烧结性能，并在低烧结温度下形成自由铅压电陶瓷组合物。 构成：用于超声波振荡器的自由铅压电陶瓷组合物由（Na0.5K0.5）NbO3组成。 添加到组合物中的添加剂含有选自Fe 2 O或NiO的0.1〜3mol％的金属氧化物和选自MnCO 3或CuO的0.1〜3mol％的金属氧化物。 由（Na0.5K0.5）NbO3组成的自由铅压电陶瓷组合物的烧结温度为1000〜1075℃。

公开(公告)号：KR1020100016887A

公开(公告)日：2010-02-16

申请号：KR1020080076534

申请日：2008-08-05

Applicant: 희성금속 주식회사 ,  (재)울산테크노파크

Inventor： 정상진 ,  태원필 ,  허대영 ,  김승민 ,  남두현

IPC: B82B3/00 ,  B82Y40/00

CPC classification number: C01G9/02 ,  B82Y30/00 ,  B82Y40/00 ,  C01P2004/64

Abstract: PURPOSE: A method for manufacturing nano zinc oxide powder is provided to synthesize various types of nano-size zinc oxide powder by varying a starting material and precipitant. CONSTITUTION: A method for manufacturing 100-200nm nano zinc oxide powder of a plate and needle shape comprises a step of performing hydrothermal treatment of Zn(NO3)2·6H2O as a starting material and NaOH as a precipitant using cyclohexylamine as a reaction controller at 200-250°C for 2-10 hours. A method for manufacturing spherical nano zinc oxide powder of 50 nm or less comprises the steps of: performing hydrothermal treatment of Zn(CH3COO)2·2H2O as a starting material and urea as a precipitant at 120-220°C for 5-12 hours; and heat treating them at 250-300°C for 12 hours.

Abstract translation: 目的：提供一种制备纳米氧化锌粉末的方法，通过改变起始原料和沉淀剂来合成各种类型的纳米尺寸氧化锌粉末。 构成：制造板状和针状的100-200nm纳米氧化锌粉末的方法包括以环己胺作为反应控制器进行水热处理Zn（NO 3）2·6H 2 O作为起始原料和NaOH作为沉淀剂的步骤 200-250℃2-10小时。 制造50nm以下的球形纳米氧化锌粉末的方法包括以下步骤：以Zn（CH 3 COO）2·2H 2 O作为原料进行水热处理，在120-220℃下进行5〜12小时的作为沉淀剂的尿素 ; 并在250-300℃下热处理12小时。

公开(公告)号：KR101108691B1

公开(公告)日：2012-01-25

申请号：KR1020080076534

申请日：2008-08-05

Applicant: 희성금속 주식회사 ,  (재)울산테크노파크

Inventor： 정상진 ,  태원필 ,  허대영 ,  김승민 ,  남두현

IPC: B82B3/00 ,  B82Y40/00

Abstract: 본 발명은 수열합성법을 이용하여 나노크기의 산화아연 분말을 제조하는 방법에 관한 것이다. Zn Nitrate를 출발물질로 하고 Precipitant를 NaOH로 하여 Cyclohexylamine(CHA)을 반응조절제로 사용하였을 경우 반응온도 200~250℃에서 Zincite 단일상의 분말을 합성하였다. 입자의 형태는 판상 또는 침상으로 100~200nm 정도의 나노 입자로 이루어져 있었다.
출발물질로 Zn Acetate를, Precipitant로 Urea를 사용하였을 경우, 반응온도 120~220℃에서 합성한 분말을 250~300℃에서 12시간 열처리해 줌으로서 단일상의 Zincite 분말을 얻을 수 있었으며 입자크기는 50nm 이하로 구형을 나타내었다.
한편, Zn Acetate의 출발물질에 Precipitant로 NaOH를 사용하였을 경우에는 반응온도 100℃~150℃의 범위에서 쉽게 Zincite 단일상을 형성하고 있으며 입자의 형태는 판상 또는 구형으로 50~200nm 정도의 나노입자를 갖는다.
수열합성법, 나노분말, 산화아연, 침상, 판상, 구상

公开(公告)号：KR101043041B1

公开(公告)日：2011-06-21

申请号：KR1020080091947

申请日：2008-09-19

Applicant: (재)울산테크노파크

Inventor： 김영혁 ,  태원필 ,  허대영 ,  지한나

IPC: H01L41/187 ,  C04B35/495 ,  C04B35/64 ,  A61H23/02

Abstract: 본 발명은 초음파 진동자용 무연 압전세라믹스 조성물에 관한 것으로서, (Na
0.5 K
0.5 )NbO
3 압전 세라믹스에 소결 첨가제 CuO, NiO, Fe
2 O
3 , MnCO
3 등을 첨가하여 소결특성을 향상시키며, 높은 기계적 품질계수(Q
m )와 높은 전기기계결합계수(k
p )를 갖는 무연 압전세라믹스 조성물을 낮은 소결 온도에서 제공하는 것에 관한 것이다.
무연 압전 세라믹스, 전기기계결합계수, 기계적 품질계수, 초음파 진동자