Abstract:
PURPOSE: A ceramic composition for a pyroelectric material is provided which can be used as a pyroelectric material acting stably at a wide range of temperature around a room temperature CONSTITUTION: A ceramic composition for pyroelectric material comprises Pb(Mg1/3Nb2/3)O3 and PbTiO3 as a main component, and additionally PbTiO3 of 30 - 40 mol%. This composition has extremely low dielectric constant, and a pyroelectric current generates at a wide range of temperature around a room temperature.
Abstract:
PURPOSE: A fabricating method of a thin film through a sol-gel technique is provided to prevent undesirable phenomena such as fracture, crack, or roughness of the thin film without employing a drying additive. CONSTITUTION: A method for fabricating a thin film through a sol-gel technique includes a step of coating a sol solution in which a film material is dissolved on a substrate or a preformed thin film, and a step of forming the thin film of gel state by drying the coated sol solution. In particular, the sol solution does not employ a drying control chemical additive. However, the sol solution has a good property of preventing fracture, crack, or roughness of the thin film. Such a property of the sol solution is obtained by controlling surface tension thereof. Surface tension of the sol solution is controlled by changing the mixture ratio between solvent and distilled water. Preferably, the sol solution may have surface tension of less than 35 dyne/cm by mixing solvent of two mol or more per one mol distilled water.
Abstract:
본 발명은 결정성 보로실리케이트계 유리프리트 및 이를 포함하는 저온 동시소성용 저유전율 유전체 세라믹 조성물에 관한 것이다. 보다 상세하게는 본 발명은 보로실리케이트계 유리프리트 기본조성에서 알칼리토류 산화물의 함량을 높게 유지하고 필요에 따라 TiO 2 등의 핵 형성제를 추가로 포함하고 있어 소성온도 800℃ 온도에서 유리 결정상이 생성되기 시작하여, 소성온도 900℃에서는 유리 결정상이 70 부피% 이상 존재하게 되는 신규 조성의 결정성 보로실리케이트계 유리프리트와, 그리고 상기한 유리프리트에 통상의 충전재를 포함시켜 750~900℃의 저온에서 소성되어 200 MPa 이상의 우수한 강도 값과 1 MHz에서의 저유전 손실율 0.1% 이하의 유전특성을 가지는 저온 동시소성(LTCC)용 저유전율 유전체 세라믹 조성물에 관한 것이다.
Abstract:
본 발명은 박테리아 및 전이금속 산화물로 이루어진 유ㆍ무기 복합체 및 이의 제조방법에 관한 것으로서, 더욱 상세하게는 높은 음전하를 나타내는 박테리아를 템플릿(template)으로 하여 박테리아 표면에 양이온의 전이금속 전구체를 부착시키고, 소듐 보로하이드라이드(sodium borohydride, NaBH 4 ) 및 상온 조건 하에서 박테리아와 전이금속 이온을 환류시켜 환원ㆍ자발 산화 반응을 유도함으로써 뛰어난 고용량의 전기화학적 특성을 갖는 박테리아 및 전이금속 산화물로 이루어진 유ㆍ무기 복합체 및 이의 제조방법에 관한 것이다. 따라서, 본 발명에 따른 유ㆍ무기복합체의 제조방법은 합성 과정의 단순화에 따른 비용 절감 및 시간 절약 효과뿐만 아니라 대량 생산이 용이하고, 저온 합성 및 균일한 나노구조체 크기, 1 차원의 형태 조절과 다른 금속 산화물에 적용이 가능하므로, 상기 유ㆍ무기복합체는 리튬 이차 전지 및 슈퍼 커패시터 등의 전기화학 분야 소자 및 나노전기 광 시스템, 촉매 분야 등에 적용이 가능하다. 박테리아, 전이금속 산화물, 유ㆍ무기 복합체, 소듐 보로하이드라이드, 고용량
Abstract:
PURPOSE: A dielectric ceramic composition for electric components is provided to include borosilicate-based glass frit and specific metal oxide and be sintered at low temperature lower than or equal to 950 degrees Celsius. CONSTITUTION: A dielectric ceramic composition for electric components includes 5-35 weight% of borosilicate-based glass frit and 65-95 weight% of composite metal oxide powder. The composite metal oxide powder is represented by chemical formula 1. In the chemical formula 1, the A is Nb, V, P, or the mixture of the same. The B is Ti, Zr, Sn, or the mixture of the same. The x, the y, and the z are the molar ratio of each oxide. The x and the y are between 20.5 and 35.5 mole%, and the z is between 29 and 59 mole%. The composition is sintered at temperature between 800 and 950 degrees Celsius. The dielectric constant of the composition in a microwave band is between 15 and 40. The quality coefficient of the composition is between 1000 and 25000GHz, and the resonance frequency temperature coefficient of the composition is between -100 and +150 ppm/degrees Celsius.
Abstract:
PURPOSE: A micro-wave dielectric ceramic composition is provided to form stacked type communication dielectric elements and modules used in a micro-wave band by mixing two or more composite metal oxide powder with borosilicate glass frit. CONSTITUTION: A micro-wave dielectric ceramic composition includes 10-30 weight% of borosilicate-based glass frit, 50-85 weight% of first composite metal oxide powder, 5-40 weight% of second composite metal oxide powder. The first composite metal oxide powder is represented by A_3B_4M_4O_21, and the second metal oxide powder is one or more selected from ZnNb_2O_6, MgTiO_3, and Li_0.5Nd_0.5TiO_3. In the A_3B_4M_4O_21, the A is Ba, Sr, or the mixture of the Ba and the Sr. The B is Ti, Zr, or the mixture of the Ti and the Zr. The M is Nb, Ta, V, or the mixture of the same. The micro-wave dielectric ceramic composition is sintered at low temperature between 850 and 900 degrees Celsius. The dielectric constant, the quality coefficient, and the resonance frequency temperature coefficient of the micro-wave dielectric ceramic composition are respectively 20 or more, 2,000 GHz or more, and between -30 and +30 ppm/degrees Celsius.
Abstract:
본 발명은 저온소성용 저유전율 세라믹 유전체 조성물에 관한 것으로서, 더욱 상세하게 설명을 하면, SiO 2 , B 2 O 3 , Al 2 O 3 , 알칼리토류 산화물 및 알칼리 금속산화물을 함유하는 보로실리케이트 유리프리트 44 ~ 65 중량%; 충전재 34 ~ 55 중량%; 및 ZrO 2 , TiO 2 , La 2 O 3 및 WO 3 중에서 선택된 단종 또는 2 종 이상의 핵 형성제 0.1 ~ 5 중량%;를 포함하는 것을 그 특징으로 한다. 본 발명의 상기 저유전율 세라믹 유전체 조성물은 800 ~ 950℃에서 저온소성이 가능하고, 상기 조성물을 이용하여 제조된 저유전율 세라믹 유전체는 4.5 ~ 6.0(1 MHz)의 낮은 유전율 및 낮은 유전손실율을 갖는 바, 신호전송속도를 증가시킬 수 있을 뿐만 아니라, 유리프리트를 부분적으로 결정화시켰기 때문에 200 MPa 이상의 기계적 강도를 갖기 때문에 내충격성이 강한 고집적 전자부품, 안테나 부품, 기판, 특히 저온 동시소성세라믹(LTCC, Low Temperature Co-fired Ceramic) 기판의 제조에 적합하다. 저온소성, 유전율, 세라믹 유전체, 유리프리트, 핵 형성제
Abstract:
본 발명은 칼슘과 코발트의 산화물을 주성분으로 하여 전기전도도 및 충·방전 용량이 우수한 신규의 칼슘-코발트 산화물계 음극활물질과, 상기 음극활물질을 특히 구연산염법으로 제조하여 고상법에 비해 균일한 입도와 미세한 입자크기를 나타내어 리튬이온 또는 고분자 이차 전지, 슈퍼 캐패시터, 열전소자 등의 전기 화학분야 소자에 적용이 가능한 음극활물질 및 이의 제조방법에 관한 것이다. 리튬 이온 이차전지, 음극활물질, 싸이클 안정성, 칼슘-코발트 산화물